Samsung Cheil Industries Infino® NH-1021 PC/ABS, Unreinforced FR

Category Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC)
Manufacturer Samsung, Cheil Industries
Trade Name Infino®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Samsung Cheil Industries Infino® NH-1021 PC/ABS, Unreinforced FR.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Information provided by Samsung Cheil Industries.
Physical Properties Metric English Comments
Specific Gravity 1.20 g/cc
1.20 g/cc
ASTM D792
Melt Flow 25 g/10 min

@Load 10.0 kg,
Temperature 220 °C
 25 g/10 min

@Load 22.0 lb,
Temperature 428 °F
 ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Rockwell R 120
120
ASTM D785
Tensile Strength at Break 66.7 MPa
9670 psi
50 mm/min; ASTM D638
Tensile Strength, Yield 62.8 MPa
9100 psi
50 mm/min; ASTM D638
Elongation at Break 96 %
96 %
50 mm/min; ASTM D638
Tensile Modulus 2.35 GPa
341 ksi
50 mm/min; ASTM D638
Flexural Strength 86.3 MPa
12500 psi
2.8 mm/min; ASTM D790
Flexural Modulus 2.26 GPa
327 ksi
2.8 mm/min; ASTM D790
Izod Impact, Notched 1.86 J/cm

@Thickness 6.35 mm
 3.49 ft-lb/in

@Thickness 0.250 in
 ASTM D256
6.86 J/cm

@Thickness 3.17 mm
 12.9 ft-lb/in

@Thickness 0.125 in
 ASTM D256
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 97.0 °C

@Thickness 6.40 mm
 207 °F

@Thickness 0.252 in
 ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 89.0 °C

@Thickness 6.40 mm
 192 °F

@Thickness 0.252 in
 ASTM D648
Vicat Softening Point 102 °C
216 °F
B/50; ISO R306
104 °C
219 °F
B/120; ISO R306
Flammability, UL94 V-0

@Thickness 1.30 mm
 V-0

@Thickness 0.0512 in