Samsung Cheil Industries Infino® LB-3150GW PC, 15% Glass Filled High Impact
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, 20% Glass Filled |
| Manufacturer | Samsung, Cheil Industries |
| Trade Name | Infino® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Samsung Cheil Industries Infino® LB-3150GW PC, 15% Glass Filled High Impact.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
High-impact resistant PC/GF that can be used for middle mold frame of LCD TVInformation provided by Samsung Cheil Industries.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.36 g/cc | 1.36 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0030 - 0.0040 cm/cm @Thickness 3.20 mm |
0.0030 - 0.0040 in/in @Thickness 0.126 in |
ASTM D955 |
| Melt Flow | 26 g/10 min @Load 10.0 kg, Temperature 250 °C |
26 g/10 min @Load 22.0 lb, Temperature 482 °F |
ASTM D1238 |
| Ash | 15 % | 15 % | ASTM D5630 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 68.6 MPa | 9950 psi | 5 mm/min; ASTM D638 |
| Tensile Strength, Yield | 68.6 MPa | 9960 psi | 5 mm/min; ASTM D638 |
| Elongation at Break | 4.3 % | 4.3 % | 5 mm/min; ASTM D638 |
| Tensile Modulus | 3.82 GPa | 555 ksi | 5 mm/min; ASTM D638 |
| Flexural Strength | 127 MPa | 18400 psi | 2.8 mm/min; ASTM D790 |
| Flexural Modulus | 4.31 GPa | 626 ksi | 2.8 mm/min; ASTM D790 |
| Izod Impact, Notched | 0.696 J/cm @Thickness 6.35 mm |
1.30 ft-lb/in @Thickness 0.250 in |
ASTM D256 |
| 0.716 J/cm @Thickness 3.17 mm |
1.34 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 142 °C @Thickness 6.40 mm |
288 °F @Thickness 0.252 in |
ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 137 °C @Thickness 6.40 mm |
279 °F @Thickness 0.252 in |
ASTM D648 |
| Vicat Softening Point | 143 °C | 289 °F | B/50; ISO R306 |
| 144 °C | 291 °F | B/120; ISO R306 | |
| Flammability, UL94 | V-2 @Thickness 3.00 mm |
V-2 @Thickness 0.118 in |
Users viewing this material also viewed the following:
- Nye Lubricants 327A (SO) Synthetic Oil
- Polymax® Maxelast® P3740 TPE, PP Overmold or Standalone use
- SABIC Innovative Plastics Lexan® 500ECR PC (Europe-Africa-Middle East)
- TSE Industries Millathane® E34 Millable Polyether Polyurethane Rubber with 60 PHR N774 (SRF) Filler
- ExxonMobil 78 Mobiltemp Series
- Arlon 55986R028 0.0295" Uncured/Cured Silicone Rubber with Fiberglass Substrate
- 3M Dyneon™ FC 2110Q Fluoroelastomer
- PolyOne Synplast™ DOA-N Di (2-ethylhexyl) Adipate
- Solvay RHODOLINE® 111 Surfactant
- PolyOne Edgetek® AM-45GF/000 PPA (Polyphthalamide), 45% Glass Fiber Reinforced, Hi-Temp (discontinued **)
Copyright © lookpolymers.com All Rights Reserved