Samsung Cheil Industries Infino® HN-1064 PC, Unreinforced FR
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, Molded |
| Manufacturer | Samsung, Cheil Industries |
| Trade Name | Infino® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Samsung Cheil Industries Infino® HN-1064 PC, Unreinforced FR.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
PC material that is applied to other resin for mobile phone chargersInformation provided by Samsung Cheil Industries.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.20 g/cc | 1.20 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm |
0.0050 - 0.0070 in/in @Thickness 0.126 in |
ASTM D955 |
| Melt Flow | 38 g/10 min @Load 10.0 kg, Temperature 250 °C |
38 g/10 min @Load 22.0 lb, Temperature 482 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 57.9 MPa | 8390 psi | 5 mm/min; ASTM D638 |
| Flexural Strength | 82.4 MPa | 12000 psi | 2.8 mm/min; ASTM D790 |
| Flexural Modulus | 2.06 GPa | 299 ksi | 2.8 mm/min; ASTM D790 |
| Izod Impact, Notched | 5.88 J/cm @Thickness 3.17 mm |
11.0 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 130 °C @Thickness 6.40 mm |
266 °F @Thickness 0.252 in |
ASTM D648 |
| Vicat Softening Point | 140 °C | 284 °F | B/50; ISO R306 |
| UL RTI, Electrical | 130 °C | 266 °F | |
| UL RTI, Mechanical with Impact | 130 °C | 266 °F | |
| UL RTI, Mechanical without Impact | 130 °C | 266 °F | |
| Flammability, UL94 | V-2 @Thickness 0.750 mm |
V-2 @Thickness 0.0295 in |
|
| V-0 @Thickness 1.50 - 3.00 mm |
V-0 @Thickness 0.0591 - 0.118 in |
Users viewing this material also viewed the following:
- Gichem GILAC D160/MT Acrylonitrile Butadiene Styrene (discontinued **)
- Albis Plastics Cellulose Acetate Butyrate B9024 (UVI, Odor Mask Added), 10% Plasticizer (discontinued **)
- Styrolution Terlux® 2812 TR MABS
- Cosmic Plastics 306 Orlon Filled Ortho Diallyl Phthalate Molding Compound
- Westlake EC812AA Low Density Polyethylene
- Trelleborg Emerson & Cuming Eccobond® 45LV Two-Component General Purpose Epoxy Adhesive
- Asahi Kasei Leona® 1302S Nylon 66
- Osprey Metals D2 Tool Steel Powder (Grade 90% - 22)
Copyright © lookpolymers.com All Rights Reserved