Samsung Cheil Industries Infino® HF-3200H PC, Glass Filled High Impact

Category Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, 10% Glass Filled
Manufacturer Samsung, Cheil Industries
Trade Name Infino®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Samsung Cheil Industries Infino® HF-3200H PC, Glass Filled High Impact.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Information provided by Samsung Cheil Industries.
Physical Properties Metric English Comments
Specific Gravity 1.37 g/cc
1.37 g/cc
ASTM D792
Melt Flow 11 g/10 min

@Load 10.0 kg,
Temperature 250 °C
 11 g/10 min

@Load 22.0 lb,
Temperature 482 °F
 ASTM D1238
Mechanical Properties Metric English Comments
Tensile Strength at Break 108 MPa
15700 psi
50 mm/min; ASTM D638
Tensile Strength, Yield 78.5 MPa
11400 psi
50 mm/min; ASTM D638
Elongation at Break 4.3 %
4.3 %
50 mm/min; ASTM D638
Tensile Modulus 4.81 GPa
697 ksi
50 mm/min; ASTM D638
Flexural Strength 118 MPa
17100 psi
2.8 mm/min; ASTM D790
Flexural Modulus 5.39 GPa
782 ksi
2.8 mm/min; ASTM D790
Izod Impact, Notched 1.47 J/cm

@Thickness 6.35 mm
 2.76 ft-lb/in

@Thickness 0.250 in
 ASTM D256
1.57 J/cm

@Thickness 3.17 mm
 2.94 ft-lb/in

@Thickness 0.125 in
 ASTM D256
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 145 °C

@Thickness 6.40 mm
 293 °F

@Thickness 0.252 in
 ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 140 °C

@Thickness 6.40 mm
 284 °F

@Thickness 0.252 in
 ASTM D648
Vicat Softening Point 147 °C
297 °F
B/50; ISO R306
150 °C
302 °F
B/120; ISO R306
Flammability, UL94 V-2

@Thickness 1.50 mm
 V-2

@Thickness 0.0591 in