- Samsung Cheil Industries Infino® GP-8200G MPPE, 20% Glass Filled
Samsung Cheil Industries Infino® GP-8200G MPPE, 20% Glass Filled
| Category | Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polyphenylene Ether, 20% Glass Filled |
| Manufacturer | Samsung, Cheil Industries |
| Trade Name | Infino® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Samsung Cheil Industries Infino® GP-8200G MPPE, 20% Glass Filled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Material with good dimensional stability and 20% GF that can be used in pumps and impeller housingsInformation provided by Samsung Cheil Industries.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.19 g/cc | 1.19 g/cc | ASTM D792 |
| Melt Flow | 7.0 g/10 min @Load 10.0 kg, Temperature 280 °C |
7.0 g/10 min @Load 22.0 lb, Temperature 536 °F |
ASTM D1238 |
| Ash | 20 % | 20 % | ASTM D5630 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 118 | 118 | ASTM D785 |
| Tensile Strength, Yield | 108 MPa | 15600 psi | 5 mm/min; ASTM D638 |
| Flexural Strength | 147 MPa | 21300 psi | 2.8 mm/min; ASTM D790 |
| Flexural Modulus | 5.88 GPa | 853 ksi | 2.8 mm/min; ASTM D790 |
| Izod Impact, Notched | 1.18 J/cm @Thickness 3.17 mm |
2.20 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 140 °C @Thickness 6.40 mm |
284 °F @Thickness 0.252 in |
ASTM D648 |
| Vicat Softening Point | 135 °C | 275 °F | B/50; ISO R306 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Yellow Index | 38 % @Thickness 3.20 mm |
38 % @Thickness 0.126 in |
ASTM D1925 |
Users viewing this material also viewed the following:
- Polymax® Maxelast® C4800 TPE, Transparent
- Nilit Nilamid B G4 FR HF 20% Glass Fiber Reinforced, Flame Retardant PA6
- Lushan PF-300 Adhesive Resin for Multi-layer Barrier Composite Sheet
- SABIC Innovative Plastics LNP THERMOCOMP MF002AS PP
- Westlake EMAC® SP2409 20% EMA Copolymer
- DuPont Elvax® 3190 Ethylene-Vinyl Acetate Copolymer Resin for Coextrusion
- Dynasol Calprene® 1204B Solution Random SBR
- Arlon 51576W015 0.0155" (0.394 mm) Uncured/Cured Silicone Rubber with Fiberglass Substrate
- Austin Novel Materials Texalan® 398A Polyester-based TPU
Copyright © lookpolymers.com All Rights Reserved