Samsung Cheil Industries Infino® EM-8250G MPPE, 20% Glass Filled

Category Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polyphenylene Ether, 20% Glass Filled
Manufacturer Samsung, Cheil Industries
Trade Name Infino®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Samsung Cheil Industries Infino® EM-8250G MPPE, 20% Glass Filled.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Information provided by Samsung Cheil Industries.
Physical Properties Metric English Comments
Specific Gravity 1.19 g/cc
1.19 g/cc
ASTM D792
Melt Flow 20 g/10 min

@Load 10.0 kg,
Temperature 280 °C
20 g/10 min

@Load 22.0 lb,
Temperature 536 °F
ASTM D1238
Ash 20 %
20 %
ASTM D5630
Mechanical Properties Metric English Comments
Tensile Strength, Yield 98.1 MPa
14200 psi
5 mm/min; ASTM D638
Flexural Strength 137 MPa
19900 psi
2.8 mm/min; ASTM D790
Flexural Modulus 5.49 GPa
797 ksi
2.8 mm/min; ASTM D790
Izod Impact, Notched 0.981 J/cm

@Thickness 3.17 mm
1.84 ft-lb/in

@Thickness 0.125 in
ASTM D256
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 128 °C

@Thickness 6.40 mm
262 °F

@Thickness 0.252 in
ASTM D648
Vicat Softening Point 135 °C
275 °F
B/50; ISO R306
Flammability, UL94 HB

@Thickness 3.00 mm
HB

@Thickness 0.118 in
Electrical Properties Metric English Comments
Surface Resistivity per Square 10000 - 1.00e+7 ohm

@Temperature 23.0 °C
10000 - 1.00e+7 ohm

@Temperature 73.4 °F
50% RH; ASTM D250
Static Decay <= 0.10 sec

@Temperature 23.0 °C
<= 0.10 sec

@Temperature 73.4 °F
50% RH; JIS L1049