- SYNTHOS Kralex® 1500 Styrene Butadiene Rubber
SYNTHOS Kralex® 1500 Styrene Butadiene Rubber
| Category | Polymer , Thermoset , Rubber or Thermoset Elastomer (TSE) |
| Manufacturer | SYNTHOS Kralupy a.s. |
| Trade Name | Kralex® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SYNTHOS Kralex® 1500 Styrene Butadiene Rubber.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
KRALEX® 1500 is a standard grade of styrene butadiene rubber. It is produced by a technology of cold emulsion polymerization based on soaps of rosin acids and contains 23.5% of chemically bonded styrene. It is coagulated by a system of acid and organic coagulant, does not contain extender oil and is stabilized by staining antioxidant.KRALEX® 1500 is appropriate for rubber compounds used in the production of car tires and inner tubes, conveyor belts, footwear, cables, hosepipes and various technical rubber articles.It is not approved for production of rubber articles coming into contact with foods or drinking water.Synthos was formerly known as Kaucuk.Synthos was formerly known as Kaucuk. All information provided by Synthos.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Volatiles | <= 0.75 % | <= 0.75 % | ASTM D5668 |
| Mooney Viscosity | 44 - 54 @Temperature 100 °C |
44 - 54 @Temperature 212 °F |
(1+4); ASTM D1646 |
| Ash | <= 0.40 % | <= 0.40 % | ASTM D5667 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 23.0 MPa | 3340 psi | 35'/145°C; ASTM D412 |
| Elongation at Break | 400 % | 400 % | 35'/145°C; ASTM D412 |
| 300% Modulus | 0.0130 - 0.0190 GPa | 1.89 - 2.76 ksi | 35'/145°C; ASTM D412 |
| Chemical Properties | Metric | English | Comments |
|---|---|---|---|
| Acid Value | 5.0 - 7.5 | 5.0 - 7.5 | ASTM D5774 |
| Styrene Content | 23.5 % | 23.5 % | ASTM D5775 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| 50% of Vulcanization t' 50 (min.) | 6.5-10.5 | ASTM D5289 |
| Antioxidant Grade | Staining | |
| Compound Safety ts 1 (min.) | 2.2-4.0 | ASTM D5289 |
| Maximal Moment (dNm) | 19-22 | ASTM D5289 |
| Minimal Moment (dNm) | 2.1-2.8 | ASTM D5289 |
| Optimal Vulcanization t' 90 (min.) | 12-17 | ASTM D5289 |
| Soaps content (%) | <= 0.3 |
Users viewing this material also viewed the following:
- Oxford Polymers 10GF 10% Glass Fiber Filled Polyetherimide for Extrusion and Injection Molding
- SABIC Innovative Plastics LNP LUBRICOMP WL004 PBT
- SABIC Innovative Plastics LNP STAT-LOY AF3009 ABS
- Solvay IGEPAL® CO 897/EP Surfactant
- Teknor Apex Monprene® MP-2235 Thermoplastic Elastomer
- A. Schulman FORMION™ FI 200 Non-Reinforced, Injection Molding Grade Ionomer / Nylon Alloy
- Dow Corning FOX® PMCP17 Flowable Oxide
- Arkema Group Orgalloy® LE 60 SF Polyamide Alloy
- BASF Paliogen® Blue L 6470 Color Additive
- Haynes 282® Nickel Alloy Plate, Solution Annealed and Age-Hardened, after long term high temperature exposure
Copyright © lookpolymers.com All Rights Reserved