SYNTHOS Forsan® 548 Acrylonitrile Butadiene Styrene (ABS)
| Category | Polymer , Thermoplastic , ABS Polymer |
| Manufacturer | SYNTHOS Kralupy a.s. |
| Trade Name | Forsan® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SYNTHOS Forsan® 548 Acrylonitrile Butadiene Styrene (ABS).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Easy flow, glossy, impact resistant.Applications: General purposeVarious technical parts, household appliances, hobby and office equipment, etc.Synthos was formerly known as Kaucuk. All information provided by Synthos.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Linear Mold Shrinkage | 0.0040 - 0.0070 cm/cm | 0.0040 - 0.0070 in/in | Internal; 50x50mm |
| Melt Flow | 21 g/10 min @Load 10.0 kg, Temperature 220 °C |
21 g/10 min @Load 22.0 lb, Temperature 428 °F |
Granulate; ISO 1133/U |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Ball Indentation Hardness | 97.0 MPa | 14100 psi | H 358/30; Ø 50x4mm; ISO 2039-1 |
| Tensile Strength at Break | 30.0 MPa @Temperature 23.0 °C |
4350 psi @Temperature 73.4 °F |
50mm/min; ISO 527-2/1A/50 |
| Tensile Strength, Yield | 38.0 MPa @Temperature 23.0 °C |
5510 psi @Temperature 73.4 °F |
50mm/min; ISO 527-2/1A/50 |
| Elongation at Break | 10 % | 10 % | 50mm/min; ISO 527-2/1A/50 |
| Tensile Modulus | 2.30 GPa @Temperature 23.0 °C |
334 ksi @Temperature 73.4 °F |
1mm/min; ISO 527-2/1A/1 |
| Flexural Strength | 60.0 MPa @Temperature 23.0 °C |
8700 psi @Temperature 73.4 °F |
2mm/min; 80x10x4mm; ISO 178 |
| Flexural Modulus | 2.10 GPa @Temperature 23.0 °C |
305 ksi @Temperature 73.4 °F |
2mm/min; 80x10x4mm; ISO 178 |
| Izod Impact, Notched (ISO) | 24.0 kJ/m² @Temperature 23.0 °C |
11.4 ft-lb/in² @Temperature 73.4 °F |
80x10x4mm, r=0.25; V-notch; ISO 180/1A |
| Charpy Impact Unnotched | 17.0 J/cm² @Temperature 23.0 °C |
80.9 ft-lb/in² @Temperature 73.4 °F |
80x10x4mm; ISO 179/1eU |
| Charpy Impact, Notched | 2.00 J/cm² @Temperature 23.0 °C |
9.52 ft-lb/in² @Temperature 73.4 °F |
80x10x4mm, r=0.25; V-notch; ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 99.0 °C | 210 °F | 80x10x4mm; ISO 75-2/Af |
| Vicat Softening Point | 95.0 °C | 203 °F | 50°C/h; 50N; 10x10x4mm; ISO 306/B50 |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
Tested in EZÚ Praha |
| Glow Wire Test | 650 °C | 1200 °F | Ø 93x3mm; IEC 60695-2-1 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 4.00e+16 ohm-cm | 4.00e+16 ohm-cm | 500V; Ø 93x3mm; IEC 60093 |
| Surface Resistance | 2.00e+16 ohm | 2.00e+16 ohm | 500V; Ø 93x3mm; IEC 60093 |
| Dielectric Constant | <= 2.7 @Frequency 50 Hz |
<= 2.7 @Frequency 50 Hz |
Ø 50x3mm; IEC 60250 |
| 2.7 @Frequency 1e+6 Hz |
2.7 @Frequency 1e+6 Hz |
Ø 50x3mm; IEC 60250 | |
| Dielectric Strength | 13.0 kV/mm @Thickness 3.00 mm |
330 kV/in @Thickness 0.118 in |
Transformer Oil; IEC 60243-1 |
| 57.0 kV/mm @Thickness 0.500 mm |
1450 kV/in @Thickness 0.0197 in |
Transformer Oil; IEC 60243-1 | |
| Dissipation Factor | 0.0040 @Frequency 50 Hz |
0.0040 @Frequency 50 Hz |
Ø 93x3mm; IEC 60250 |
| 0.0080 @Frequency 1e+6 Hz |
0.0080 @Frequency 1e+6 Hz |
Ø 93x3mm; IEC 60250 | |
| Arc Resistance | 89 sec | 89 sec | Ø 93x3mm; IEC 61621 |
| Comparative Tracking Index | 400 V | 400 V | Solution A; Ø 93x3mm; IEC 60112 |