SYNTHOS Forsan® 449 Acrylonitrile Butadiene Styrene (ABS)

Category Polymer , Thermoplastic , ABS Polymer
Manufacturer SYNTHOS Kralupy a.s.
Trade Name Forsan®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SYNTHOS Forsan® 449 Acrylonitrile Butadiene Styrene (ABS).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
High flow, high gloss, suitable for electroplating.Applications: General purpose, intricate and thin-walled productsHousehold appliances, vacuum cleaners, heels, toys, fan grilles, etc.Synthos was formerly known as Kaucuk. All information provided by Synthos.
Physical Properties Metric English Comments
Linear Mold Shrinkage 0.0040 - 0.0070 cm/cm
0.0040 - 0.0070 in/in
Internal; 50x50mm
Melt Flow 32.55 g/10 min

@Load 10.0 kg,
Temperature 220 °C
32.55 g/10 min

@Load 22.0 lb,
Temperature 428 °F
Granulate; ISO 1133/U
Mechanical Properties Metric English Comments
Ball Indentation Hardness 99.0 MPa
14400 psi
H 358/30; Ø 50x4mm; ISO 2039-1
Tensile Strength at Break 32.0 MPa

@Temperature 23.0 °C
4640 psi

@Temperature 73.4 °F
50mm/min; ISO 527-2/1A/50
Tensile Strength, Yield 40.0 MPa

@Temperature 23.0 °C
5800 psi

@Temperature 73.4 °F
50mm/min; ISO 527-2/1A/50
Elongation at Break 12 %
12 %
50mm/min; ISO 527-2/1A/50
Tensile Modulus 2.50 GPa

@Temperature 23.0 °C
363 ksi

@Temperature 73.4 °F
1mm/min; ISO 527-2/1A/1
Flexural Strength 62.0 MPa

@Temperature 23.0 °C
8990 psi

@Temperature 73.4 °F
2mm/min; 80x10x4mm; ISO 178
Flexural Modulus 2.30 GPa

@Temperature 23.0 °C
334 ksi

@Temperature 73.4 °F
2mm/min; 80x10x4mm; ISO 178
Izod Impact, Notched (ISO) 19.0 kJ/m²

@Temperature 23.0 °C
9.04 ft-lb/in²

@Temperature 73.4 °F
80x10x4mm, r=0.25; V-notch; ISO 180/1A
Charpy Impact Unnotched 13.0 J/cm²

@Temperature 23.0 °C
61.9 ft-lb/in²

@Temperature 73.4 °F
80x10x4mm; ISO 179/1eU
Charpy Impact, Notched 1.60 J/cm²

@Temperature 23.0 °C
7.61 ft-lb/in²

@Temperature 73.4 °F
80x10x4mm, r=0.25; V-notch; ISO 179/1eA
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 94.0 °C
201 °F
80x10x4mm; ISO 75-2/Af
Vicat Softening Point 95.0 °C
203 °F
50°C/h; 50N; 10x10x4mm; ISO 306/B50
Flammability, UL94 HB

@Thickness 1.60 mm
HB

@Thickness 0.0630 in
Tested in EZÚ Praha
Glow Wire Test 650 °C
1200 °F
Ø 93x3mm; IEC 60695-2-1
Electrical Properties Metric English Comments
Volume Resistivity 4.00e+16 ohm-cm
4.00e+16 ohm-cm
500V; Ø 93x3mm; IEC 60093
Surface Resistance 1.00e+16 ohm
1.00e+16 ohm
500V; Ø 93x3mm; IEC 60093
Dielectric Constant 2.6

@Frequency 1e+6 Hz
2.6

@Frequency 1e+6 Hz
Ø 50x3mm; IEC 60250
<= 2.7

@Frequency 50 Hz
<= 2.7

@Frequency 50 Hz
Ø 50x3mm; IEC 60250
Dielectric Strength 13.0 kV/mm

@Thickness 3.00 mm
330 kV/in

@Thickness 0.118 in
Transformer Oil; IEC 60243-1
53.0 kV/mm

@Thickness 0.500 mm
1350 kV/in

@Thickness 0.0197 in
Transformer Oil; IEC 60243-1
Dissipation Factor 0.0040

@Frequency 50 Hz
0.0040

@Frequency 50 Hz
Ø 93x3mm; IEC 60250
0.0080

@Frequency 1e+6 Hz
0.0080

@Frequency 1e+6 Hz
Ø 93x3mm; IEC 60250
Arc Resistance 82 sec
82 sec
Ø 93x3mm; IEC 61621
Comparative Tracking Index 400 V
400 V
Solution A; Ø 93x3mm; IEC 60112