SCG Chemicals EL-Proâ„¢ P700J Polypropylene Injection Molding
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Molded |
| Manufacturer | SCG Chemicals Co. |
| Trade Name | EL-Pro™ |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SCG Chemicals EL-Proâ„¢ P700J Polypropylene Injection Molding.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Key Characteristics:High stiffnessHigh glossHigh productivityGood processabilityOdorlessSafe for food contactRecommended Applications:General purpose housewaresFood containersMedical instrumentsInfant articles, toysOffice accessoriesInformation provided by SCG Chemicals
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.910 g/cc | 0.910 g/cc | ASTM D1505 |
| Linear Mold Shrinkage, Flow | 0.012 cm/cm @Thickness 2.00 mm |
0.012 in/in @Thickness 0.0787 in |
TPE Method |
| Linear Mold Shrinkage, Transverse | 0.012 cm/cm @Thickness 2.00 mm |
0.012 in/in @Thickness 0.0787 in |
TPE Method |
| Melt Flow | 12 g/10 min @Load 2.16 kg, Temperature 230 °C |
12 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 90 | 90 | ASTM D785 |
| Tensile Strength at Break | 20.0 MPa | 2900 psi | ASTM D638 |
| Tensile Strength, Yield | 31.4 MPa | 4550 psi | ASTM D638 |
| Elongation at Break | 650 % | 650 % | ASTM D638 |
| Flexural Modulus | 1.42 GPa | 206 ksi | ASTM D790 |
| Izod Impact, Notched | 0.196 J/cm @Temperature 0.000 °C |
0.367 ft-lb/in @Temperature 32.0 °F |
ASTM D256 |
| 0.294 J/cm @Temperature 23.0 °C |
0.551 ft-lb/in @Temperature 73.4 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 163 °C | 325 °F | ASTM D2117 |
| Deflection Temperature at 0.46 MPa (66 psi) | 110 °C | 230 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 65.0 °C | 149 °F | ASTM D648 |
| Vicat Softening Point | 155 °C | 311 °F | ASTM D1525 |
| Brittleness Temperature | -20.0 °C | -4.00 °F | ASTM D746 |
| Flammability, UL94 | HB | HB |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | 47 % @Thickness 1.00 mm |
47 % @Thickness 0.0394 in |
ASTM D1003 |
| Gloss | 51 % @Thickness 1.00 mm |
51 % @Thickness 0.0394 in |
ASTM D2457 |
Users viewing this material also viewed the following:
- Resirene Resirene® READ 9500 Ignition Resistant Impact Polystyrene
- SABIC Innovative Plastics LNP LUBRICOMP RFL26 PA 66
- The NanoSteel® Company SHS 7574 HVOF Steel Alloy, Atomized Powder
- ExxonMobil Mobil Rarus 829
- Eastman Tritan MX711 Copolyester
- Crucible Compaction Metals P/M Low Carbon Astroloy, Supersolvus
- Arkema Group Orgalloy® LE 6000 Polyamide 6 Alloy
- UBE UBEPOL BR15HB HIPS (n-DM = 0.03 wt % and PH-3H = 0.03 wt %)
Copyright © lookpolymers.com All Rights Reserved