SCG Chemicals EL-Leneâ„¢ LD1905F Low Density Polyethylene Film

Category Polymer , Film , Thermoplastic , Polyethylene (PE) , LDPE , Low Density Polyethylene (LDPE), Film Grade
Manufacturer SCG Chemicals Co.
Trade Name EL-Lene™
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SCG Chemicals EL-Leneâ„¢ LD1905F Low Density Polyethylene Film.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Key Characteristics:High productivityGood optical propertiesCan be blended with HDPE, LLDPEContains 1500 ppm slip agent and 2600 ppm antiblocking agentRecommended Applications:General purpose bagVegetable and fruit bagFoam, bubble sheet, shoe soleInformation provided by SCG Chemicals
Physical Properties Metric English Comments
Specific Gravity 0.919 g/cc
0.919 g/cc
ASTM D1505
Thickness 38.0 microns
1.50 mil
Melt Flow 5.0 g/10 min

@Load 2.16 kg,
Temperature 190 °C
5.0 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ASTM D1238
Mechanical Properties Metric English Comments
Film Tensile Strength at Yield, TD 10.0 MPa
1450 psi
ASTM D882
Film Elongation at Break, MD 400 %
400 %
ASTM D882
Film Elongation at Break, TD 700 %
700 %
ASTM D882
Secant Modulus, MD 0.170 GPa
24.7 ksi
ASTM D882
Secant Modulus, TD 0.190 GPa
27.6 ksi
ASTM D882
Elmendorf Tear Strength, MD 15.7 g/micron
400 g/mil
ASTM D1922
Elmendorf Tear Strength, TD 10.8 g/micron
275 g/mil
ASTM D1922
Dart Drop 3.40 g/micron
86.4 g/mil
ASTM D1709
Dart Drop Test 130 g
0.287 lb
ASTM D1709
Film Tensile Strength at Break, MD 20.0 MPa
2900 psi
ASTM D882
Film Tensile Strength at Break, TD 15.0 MPa
2180 psi
ASTM D882
Thermal Properties Metric English Comments
Melting Point 110 °C
230 °F
ASTM D2117
Vicat Softening Point 92.0 °C
198 °F
ASTM D1525
Brittleness Temperature <= -74.0 °C
<= -101 °F
ASTM D746
Optical Properties Metric English Comments
Haze 7.0 %
7.0 %
ASTM D1003
Gloss 55 %
55 %
ASTM D2457