SCG Chemicals EL-Leneâ„¢ H6007JU High Density Polyethylene Injection Molding
| Category | Polymer , Thermoplastic , Polyethylene (PE) , HDPE , High Density Polyethylene (HDPE), Injection Molded |
| Manufacturer | SCG Chemicals Co. |
| Trade Name | EL-Lene™ |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SCG Chemicals EL-Leneâ„¢ H6007JU High Density Polyethylene Injection Molding.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Key Characteristics:Good processabilityHigh rigidityHigh impact resistanceGood weathering resistance (UV stabilizer)Recommended Applications:Crates for soft drink, bottles, pallet, garbage bins, containersIndustrial parts for outdoor uses such as motorcycle fendersInformation provided by SCG Chemicals
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.964 g/cc | 0.964 g/cc | ASTM D1505 |
| Environmental Stress Crack Resistance | 4.0 hour @Temperature 50.0 °C |
4.0 hour @Temperature 122 °F |
F50, 25% Igepal; ASTM D1693 |
| Linear Mold Shrinkage, Flow | 0.0155 cm/cm @Thickness 2.00 mm |
0.0155 in/in @Thickness 0.0787 in |
TPE Method |
| Linear Mold Shrinkage, Transverse | 0.0096 cm/cm @Thickness 2.00 mm |
0.0096 in/in @Thickness 0.0787 in |
TPE Method |
| Melt Flow | 7.5 g/10 min @Load 2.16 kg, Temperature 190 °C |
7.5 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 68 | 68 | ASTM D2240 |
| Tensile Strength at Break | 30.0 MPa | 4350 psi | ASTM D638 |
| Tensile Strength, Yield | 30.4 MPa | 4410 psi | ASTM D638 |
| Elongation at Break | 1000 % | 1000 % | ASTM D638 |
| Flexural Modulus | 1.32 GPa | 192 ksi | ASTM D790 |
| Izod Impact, Notched | >= 0.343 J/cm @Temperature 23.0 °C |
>= 0.643 ft-lb/in @Temperature 73.4 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 133 °C | 271 °F | ASTM D2117 |
| Deflection Temperature at 0.46 MPa (66 psi) | 75.0 °C | 167 °F | ASTM D648 |
| Vicat Softening Point | 127 °C | 261 °F | ASTM D1525 |
| Brittleness Temperature | -60.0 °C | -76.0 °F | ASTM D746 |