- High Density Polyethylene (HDPE), Injection Molded
- SCG Chemicals EL-Leneâ„¢ H5814J High Density Polyethylene Injection Molding
SCG Chemicals EL-Leneâ„¢ H5814J High Density Polyethylene Injection Molding
| Category | Polymer , Thermoplastic , Polyethylene (PE) , HDPE , High Density Polyethylene (HDPE), Injection Molded |
| Manufacturer | SCG Chemicals Co. |
| Trade Name | EL-Lene™ |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SCG Chemicals EL-Leneâ„¢ H5814J High Density Polyethylene Injection Molding.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Key Characteristics:Good processabilityHigh stiffnessHigh impact strengthBalanced properties between shrinkage and warpageOdorlessSafe for food contactRecommended Applications: General purpose injection parts such as utensils, office articles, bottle caps, toy partsInformation provided by SCG Chemicals
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.958 g/cc | 0.958 g/cc | ASTM D1505 |
| Environmental Stress Crack Resistance | 2.0 hour @Temperature 50.0 °C |
2.0 hour @Temperature 122 °F |
F50, 25% Igepal; ASTM D1693 |
| Linear Mold Shrinkage, Flow | 0.016 cm/cm @Thickness 2.00 mm |
0.016 in/in @Thickness 0.0787 in |
TPE Method |
| Linear Mold Shrinkage, Transverse | 0.0177 cm/cm @Thickness 2.00 mm |
0.0177 in/in @Thickness 0.0787 in |
TPE Method |
| Melt Flow | 14 g/10 min @Load 2.16 kg, Temperature 190 °C |
14 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 65 | 65 | ASTM D2240 |
| Tensile Strength at Break | 27.0 MPa | 3920 psi | ASTM D638 |
| Tensile Strength, Yield | 17.7 MPa | 2560 psi | ASTM D638 |
| Elongation at Break | 620 % | 620 % | ASTM D638 |
| Flexural Modulus | 1.23 GPa | 178 ksi | ASTM D790 |
| Izod Impact, Notched | >= 0.294 J/cm @Temperature 23.0 °C |
>= 0.551 ft-lb/in @Temperature 73.4 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 131 °C | 268 °F | ASTM D2117 |
| Deflection Temperature at 0.46 MPa (66 psi) | 75.0 °C | 167 °F | ASTM D648 |
| Vicat Softening Point | 122 °C | 252 °F | ASTM D1525 |
| Brittleness Temperature | -60.0 °C | -76.0 °F | ASTM D746 |
| Flammability, UL94 | HB | HB |