SCG Chemicals EL-Leneâ„¢ D682PC Low Density Polyethylene Pipe Resin
| Category | Polymer , Thermoplastic , Polyethylene (PE) , LDPE , Low Density Polyethylene (LDPE), Extrusion Grade |
| Manufacturer | SCG Chemicals Co. |
| Trade Name | EL-Lene™ |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SCG Chemicals EL-Leneâ„¢ D682PC Low Density Polyethylene Pipe Resin.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Key Characteristics: High flexibility, good processingRecommended Applications: Irrigation pipesInformation provided by SCG Chemicals
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.939 g/cc | 0.939 g/cc | ISO 1183 |
| Environmental Stress Crack Resistance | >= 10000 hour | >= 10000 hour | F0; ASTM D1693 |
| Oxidative Induction Time (OIT) | >= 40 min @Temperature 200 °C |
>= 40 min @Temperature 392 °F |
ISO/TR10837 |
| Carbon Black Loading | 2.3 % | 2.3 % | ISO 6964 |
| Melt Flow | 0.18 g/10 min @Load 5.00 kg, Temperature 190 °C |
0.18 g/10 min @Load 11.0 lb, Temperature 374 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | >= 18.0 MPa | >= 2610 psi | Crosshead speed 100 mm/min; ISO 527 |
| Elongation at Break | >= 600 % | >= 600 % | Crosshead speed 100 mm/min; ISO 527 |
| Hydrostatic Design Basis | 5.00 MPa | 725 psi | MRS Classified; ISO 9080 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Brittleness Temperature | <= -60.0 °C | <= -76.0 °F | ASTM D746 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Carbon Black/Pigment Dispersion (grade) | <3 | ISO 18553 |
| Color | Black |
Users viewing this material also viewed the following:
- Nylene® 409 Nylon 6
- Kazanorgsintez 153-15 Composition of Low Density Polyethylene, Crack-Proof
- A. Schulman COMTUF® 506 Polycarbonate
- A. Schulman POLYBATCH™ AC-20531L UV Absorber Concentrate
- Eurostar Staramide PFB42EU PA6, Glass Fiber/Bead Filled, Injection Molded
- Arlon 26122P020 0.020" Cured Silicone Rubber/Laminated PTFE Film
- 3M Scotchlite™ 680-81 Reflective Graphic Film
- Axiall 7801 Rigid PVC, Extrusion, White, High Impact Profile
- Arkema Group Lacovyl® EF 701 PVC
- Arkema Group KYNAR® 9000 HD Polyvinylidene Fluoride - Injection Molding
Copyright © lookpolymers.com All Rights Reserved