SABIC PP 523P Polypropylene Homopolymer for Bi-axially Oriented Film

Category Polymer , Film , Thermoplastic , Polypropylene (PP) , Polypropylene, Film Grade
Manufacturer SABIC
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC PP 523P Polypropylene Homopolymer for Bi-axially Oriented Film.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Product Description: PP 523P is a non formulated grade, specially developed for bi-axially oriented PP (BOPP) film extrusion with a very specific molecular structure providing ultimate properties required for the stenter film process. PP 523P is suitable for metallizable film, both as monolayer and in co-extruded structures.Films produced using PP 523P will exhibit:Consistent processabilityVery good film profileExcellent optical propertiesHigh tensile propertiesLow residual ashFilm produced can be metalizedTypical Applications: PP 523P can be used as core layer in co-extruded film and/or as base material for plain films used for stationary, dry food bags, synthetic paper and heat sealable packaging films.Information provided by SABIC.
Physical Properties Metric English Comments
Density 0.905 g/cc
0.0327 lb/in³
ASTM D792
Melt Flow 3.0 g/10 min

@Load 2.16 kg,
Temperature 230 °C
3.0 g/10 min

@Load 4.76 lb,
Temperature 446 °F
ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Rockwell R 105
105
ASTM D785
Tensile Strength, Yield 35.0 MPa
5080 psi
ASTM D638
Elongation at Yield 12 %
12 %
ASTM D638
Flexural Modulus, 1% Secant 1500 MPa
218000 psi
ASTM D790A
Izod Impact, Notched 0.350 J/cm
0.656 ft-lb/in
ASTM D256
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 94.0 °C
201 °F
ASTM D648
Vicat Softening Point 156 °C
313 °F
ASTM D1525B
Processing Properties Metric English Comments
Processing Temperature 245 - 255 °C
473 - 491 °F
Barrel Temperature