SABIC PP 413MNK45 Polypropylene Impact Copolymer for Injection Molding

Category Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Impact Modified; Molded/Extruded
Manufacturer SABIC
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC PP 413MNK45 Polypropylene Impact Copolymer for Injection Molding.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Product Description: PP 413MNK45 is a controlled rheology PP grade with a very high fluidity. It is provided with an antistatic package & nucleating agent and is especially developed for producing injection molded articles. This grade has a good impact resistance (even at low temperature) and high stiffness.Typical Applications: PP 413MNK45 can be used for housewares and thin wall packaging containers (e.g. margarine tubs, yogurt pots and ice cream containers, etc.).Information provided by SABIC.
Physical Properties Metric English Comments
Density 0.905 g/cc
0.0327 lb/in³
ASTM D792
Linear Mold Shrinkage 0.012 - 0.025 cm/cm
0.012 - 0.025 in/in
Melt Flow 70 g/10 min

@Load 2.16 kg,
Temperature 230 °C
70 g/10 min

@Load 4.76 lb,
Temperature 446 °F
ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Rockwell R 94
94
ASTM D785
Tensile Strength, Yield 28.0 MPa
4060 psi
ASTM D638
Elongation at Yield 5.0 %
5.0 %
ASTM D638
Flexural Modulus, 1% Secant 1550 MPa
225000 psi
ASTM D790A
Izod Impact, Notched 0.350 J/cm

@Temperature -20.0 °C
0.656 ft-lb/in

@Temperature -4.00 °F
ASTM D256
0.650 J/cm

@Temperature 23.0 °C
1.22 ft-lb/in

@Temperature 73.4 °F
ASTM D256
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 95.0 °C
203 °F
ASTM D648
Vicat Softening Point 150 °C
302 °F
ASTM D1525B
Processing Properties Metric English Comments
Processing Temperature 200 - 235 °C
392 - 455 °F
Barrel Temperature
Mold Temperature 15.0 - 40.0 °C
59.0 - 104 °F