SABIC Innovative Plastics Xylex X7529 PC+POLYESTER (Europe-Africa-Middle East)

Category	Polymer , Thermoplastic , Polycarbonate (PC) , Polyester, TP
Manufacturer	SABIC Innovative Plastics (GE Plastics)
Trade Name	Xylex
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	SABIC Innovative Plastics Xylex X7529 PC+POLYESTER (Europe-Africa-Middle East).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

PC+ POLYESTER unreinforced alloy developed for optical or lense market. Good flow with good impact and excellent optical quality. UV 400nm block.This data was supplied by SABIC-IP for the Europe-Africa-Middle East region.

Physical Properties	Metric	English	Comments
Specific Gravity	1.20 g/cc	1.20 g/cc	ASTM D 792
Density	1.20 g/cc	0.0434 lb/inÂ³	ISO 1183
Moisture Absorption at Equilibrium	0.14 %	0.14 %	23Â°C / 50% RH; ISO 62
Water Absorption at Saturation	0.16 % @Temperature 23.0 Â°C	0.16 % @Temperature 73.4 Â°F	ISO 62
Linear Mold Shrinkage, Flow	0.0040 - 0.0060 cm/cm @Thickness 3.20 mm	0.0040 - 0.0060 in/in @Thickness 0.126 in	SABIC Method
Melt Flow	11 g/10 min @Load 2.16 kg, Temperature 265 Â°C	11 g/10 min @Load 4.76 lb, Temperature 509 Â°F	[cm^3/10 min] Melt Volume Rate; ISO 1133
	12 g/10 min @Load 2.16 kg, Temperature 265 Â°C	12 g/10 min @Load 4.76 lb, Temperature 509 Â°F	ASTM D 1238

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	62.0 MPa	8990 psi	50 mm/min; ISO 527
	63.0 MPa	9140 psi	Type I, 50 mm/min; ASTM D 638
Tensile Strength, Yield	60.0 MPa	8700 psi	Type I, 50 mm/min; ASTM D 638
	60.0 MPa	8700 psi	50 mm/min; ISO 527
Elongation at Break	133 %	133 %	50 mm/min; ISO 527
	135 %	135 %	Type I, 50 mm/min; ASTM D 638
Elongation at Yield	5.8 %	5.8 %	50 mm/min; ISO 527
	6.3 %	6.3 %	Type I, 50 mm/min; ASTM D 638
Tensile Modulus	2.14 GPa	310 ksi	50 mm/min; ASTM D 638
	2.30 GPa	334 ksi	1 mm/min; ISO 527
Flexural Strength	92.0 MPa	13300 psi	2 mm/min; ISO 178
Flexural Yield Strength	95.0 MPa	13800 psi	1.3 mm/min, 50 mm span; ASTM D 790
Flexural Modulus	2.25 GPa	326 ksi	2 mm/min; ISO 178
	2.30 GPa	334 ksi	1.3 mm/min, 50 mm span; ASTM D 790
Izod Impact, Notched	0.100 J/cm @Temperature -30.0 Â°C	0.187 ft-lb/in @Temperature -22.0 Â°F	ASTM D 256
	5.20 J/cm @Temperature 23.0 Â°C	9.74 ft-lb/in @Temperature 73.4 Â°F	ASTM D 256
Izod Impact, Notched (ISO)	6.00 kJ/mÂ² @Temperature -30.0 Â°C	2.86 ft-lb/inÂ² @Temperature -22.0 Â°F	80104; ISO 180/1A
	9.00 kJ/mÂ² @Temperature 23.0 Â°C	4.28 ft-lb/inÂ² @Temperature 73.4 Â°F	80104; ISO 180/1A
Charpy Impact, Notched	1.00 J/cmÂ² @Temperature 23.0 Â°C	4.76 ft-lb/inÂ² @Temperature 73.4 Â°F	V-notch Edgew 80104 sp=62mm; ISO 179/1eA
Impact Test	70.0 J @Temperature 23.0 Â°C	51.6 ft-lb @Temperature 73.4 Â°F	Instrumented Impact Total Energy; ASTM D 3763

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	90.0 Âµm/m-Â°C @Temperature 23.0 - 60.0 Â°C	50.0 Âµin/in-Â°F @Temperature 73.4 - 140 Â°F	ISO 11359-2
	104 Âµm/m-Â°C @Temperature -40.0 - 40.0 Â°C	57.8 Âµin/in-Â°F @Temperature -40.0 - 104 Â°F	ASTM E 831
CTE, linear, Transverse to Flow	90.0 Âµm/m-Â°C @Temperature 23.0 - 60.0 Â°C	50.0 Âµin/in-Â°F @Temperature 73.4 - 140 Â°F	ISO 11359-2
	104 Âµm/m-Â°C @Temperature -40.0 - 40.0 Â°C	57.8 Âµin/in-Â°F @Temperature -40.0 - 104 Â°F	ASTM E 831
Deflection Temperature at 0.46 MPa (66 psi)	119 Â°C @Thickness 3.20 mm	246 Â°F @Thickness 0.126 in	unannealed; ASTM D 648
Deflection Temperature at 1.8 MPa (264 psi)	106 Â°C	223 Â°F	Edgew 120104 sp=100mm; ISO 75/Ae
	106 Â°C @Thickness 3.20 mm	223 Â°F @Thickness 0.126 in	unannealed; ASTM D 648
Vicat Softening Point	124 Â°C	255 Â°F	Rate B/50; ISO 306
	126 Â°C	259 Â°F	Rate B/120; ISO 306
	126 Â°C	259 Â°F	Rate B/50; ASTM D 1525

Optical Properties	Metric	English	Comments
Haze	2.0 % @Thickness 2.54 mm	2.0 % @Thickness 0.100 in	ASTM D 1003
Transmission, Visible	86 % @Thickness 2.54 mm	86 % @Thickness 0.100 in	ASTM D 1003

Users viewing this material also viewed the following: