SABIC Innovative Plastics Xenoy® XLG2400 PC+PET

Category Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name Xenoy®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics Xenoy® XLG2400 PC+PET.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Low Gloss Xenoy, providing inherent low gloss on almLow Gloss Xenoy, providing inherent low gloss on almost every type of tool surfaces. This grade has excellent low temperature impact, high heat resistant and is UV stabilized. Many colors available. Pls refer to the low gloss processing guidelines for optimal low gloss.
Physical Properties Metric English Comments
Specific Gravity 1.19 g/cc
1.19 g/cc
ASTM D792
Density 1.19 g/cc
0.0430 lb/in³
ISO 1183
Moisture Absorption 0.0800 %
0.0800 %
23°C / 50% RH; ISO 62
Water Absorption at Saturation 0.080 %
0.080 %
ISO 62
Linear Mold Shrinkage, Flow 0.0080 - 0.010 cm/cm

@Thickness 3.20 mm
0.0080 - 0.010 in/in

@Thickness 0.126 in
SABIC Method
Melt Flow 17.5 g/10 min

@Load 5.00 kg,
Temperature 266 °C
17.5 g/10 min

@Load 11.0 lb,
Temperature 511 °F
ASTM D1238
Melt Index of Compound 17 g/10 min

@Load 5.00 kg,
Temperature 265 °C
17 g/10 min

@Load 11.0 lb,
Temperature 509 °F
MVR [cm^3/10 min]; ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break 44.0 MPa
6380 psi
Type I, 50 mm/min; ASTM D638
47.0 MPa
6820 psi
50 mm/min; ISO 527
Tensile Strength, Yield 43.0 MPa
6240 psi
Type I, 50 mm/min; ASTM D638
45.0 MPa
6530 psi
50 mm/min; ISO 527
Elongation at Break 103 %
103 %
Type I, 50 mm/min; ASTM D638
122.3 %
122.3 %
50 mm/min; ISO 527
Elongation at Yield 4.6 %
4.6 %
50 mm/min; ISO 527
5.1 %
5.1 %
Type I, 50 mm/min; ASTM D638
Tensile Modulus 1.73 GPa
251 ksi
5 mm/min; ASTM D638
1.94 GPa
281 ksi
1 mm/min; ISO 527
Flexural Yield Strength 67.0 MPa
9720 psi
1.3 mm/min, 50 mm span; ASTM D790
68.0 MPa
9860 psi
2 mm/min; ISO 178
Flexural Modulus 1.77 GPa
257 ksi
2 mm/min; ISO 178
1.85 GPa
268 ksi
1.3 mm/min, 50 mm span; ASTM D790
Izod Impact, Notched 5.78 J/cm
10.8 ft-lb/in
ASTM D256
5.13 J/cm

@Temperature -30.0 °C
9.61 ft-lb/in

@Temperature -22.0 °F
ASTM D256
Izod Impact, Notched (ISO) 47.0 kJ/m²
22.4 ft-lb/in²
80*10*4; ISO 180/1A
40.0 kJ/m²

@Temperature -30.0 °C
19.0 ft-lb/in²

@Temperature -22.0 °F
80*10*4; ISO 180/1A
Charpy Impact, Notched 5.20 J/cm²
24.7 ft-lb/in²
Edgew 80*10*4 sp=62mm; ISO 179/1eA
Dart Drop, Total Energy 40.0 J

@Temperature 23.0 °C
29.5 ft-lb

@Temperature 73.4 °F
ASTM D3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 76.6 µm/m-°C

@Temperature -40.0 - 40.0 °C
42.6 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
76.6 µm/m-°C

@Temperature -40.0 - 40.0 °C
42.6 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
CTE, linear, Transverse to Flow 97.9 µm/m-°C

@Temperature -40.0 - 40.0 °C
54.4 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
97.9 µm/m-°C

@Temperature -40.0 - 40.0 °C
54.4 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
Deflection Temperature at 1.8 MPa (264 psi) 97.0 °C
207 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
102 °C

@Thickness 3.20 mm
216 °F

@Thickness 0.126 in
unannealed; ASTM D648
Vicat Softening Point 128 °C
262 °F
Rate B/120; ISO 306
129 °C
264 °F
Rate B/50; ASTM D1525
129 °C
264 °F
Rate B/50; ISO 306