- SABIC Innovative Plastics Xenoy® X5630Q PC+PET (Europe-Africa-Middle East)
SABIC Innovative Plastics Xenoy® X5630Q PC+PET (Europe-Africa-Middle East)
| Category | Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Xenoy® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics Xenoy® X5630Q PC+PET (Europe-Africa-Middle East).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Mineral filled PC/PET blend with high heat dimensional stability, low shrinkage and low CTE, especially for painted applications
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.35 g/cc | 0.0488 lb/in³ | ISO 1183 |
| Moisture Absorption | 0.140 % | 0.140 % | 23°C / 50% RH; ISO 62 |
| Water Absorption at Saturation | 0.42 % | 0.42 % | ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0070 cm/cm | 0.0050 - 0.0070 in/in | on Tensile Bar; SABIC Method |
| Melt Index of Compound | 15 g/10 min @Load 5.00 kg, Temperature 265 °C |
15 g/10 min @Load 11.0 lb, Temperature 509 °F |
MVR [cm^3/10 min]; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 50.0 MPa | 7250 psi | 5 mm/min; ISO 527 |
| Tensile Strength, Yield | 56.0 MPa | 8120 psi | 5 mm/min; ISO 527 |
| Elongation at Break | 8.0 % | 8.0 % | 5 mm/min; ISO 527 |
| Elongation at Yield | 3.2 % | 3.2 % | 5 mm/min; ISO 527 |
| Tensile Modulus | 4.15 GPa | 602 ksi | 1 mm/min; ISO 527 |
| Flexural Yield Strength | 90.0 MPa | 13100 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 4.05 GPa | 587 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 8.00 kJ/m² | 3.81 ft-lb/in² | 80*10*4; ISO 180/1A |
| 6.00 kJ/m² @Temperature -30.0 °C |
2.86 ft-lb/in² @Temperature -22.0 °F |
80*10*4; ISO 180/1A | |
| Izod Impact, Unnotched (ISO) | 100 kJ/m² | 47.6 ft-lb/in² | 80*10*4; ISO 180/1U |
| 80.0 kJ/m² @Temperature -30.0 °C |
38.1 ft-lb/in² @Temperature -22.0 °F |
80*10*4; ISO 180/1U | |
| Charpy Impact, Notched | 0.800 J/cm² | 3.81 ft-lb/in² | Edgew 80*10*4 sp=62mm; ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 52.0 µm/m-°C @Temperature -30.0 - 80.0 °C |
28.9 µin/in-°F @Temperature -22.0 - 176 °F |
ISO 11359-2 |
| CTE, linear, Transverse to Flow | 72.0 µm/m-°C @Temperature -30.0 - 80.0 °C |
40.0 µin/in-°F @Temperature -22.0 - 176 °F |
ISO 11359-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 110 °C | 230 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| Vicat Softening Point | 137 °C | 279 °F | Rate B/50; ISO 306 |
| 140 °C | 284 °F | Rate B/120; ISO 306 |
Users viewing this material also viewed the following:
- Plastcom SLOVAMID 6 GF 15 T 25 TS PA6, 15% glass fibre, 25% mineral filling
- Solvay Specialty Polymers AvaSpire® AV-651 Polyaryletherketone (PAEK)
- Stir SpA T 4080 A (PVC)
- Chase Plastics CP Pryme® N333GL (DAM) Nylon 6 (Utility Grade), 33% Glass Fiber Reinforced, Internally Lubricated
- Cosmic Plastics 6220 Short Glass Fiber Filled Iso Diallyl Phthalate Molding Compound
- American Elements Erbium Oxide Nanopowder
- Chi Mei Wonderlite® PC-115 Polycarbonate
- Diamond Polymers ASA S150
- Arlon 25FR Low-Cost Ceramic Hydrocarbon
- Weartech International WT-25 Cobalt Hardfacing & Wear Resistant Alloy
Copyright © lookpolymers.com All Rights Reserved