SABIC Innovative Plastics Xenoy® X5630 PC+PET (Europe-Africa-Middle East)

Category	Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC)
Manufacturer	SABIC Innovative Plastics (GE Plastics)
Trade Name	Xenoy®
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	SABIC Innovative Plastics Xenoy® X5630 PC+PET (Europe-Africa-Middle East).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Mineral filled PC/PET blend with high heat dimensional stability, low shrinkage and low CTE, especially for painted applications

Physical Properties	Metric	English	Comments
Specific Gravity	1.35 g/cc	1.35 g/cc	ASTM D792
Density	1.35 g/cc	0.0488 lb/in³	ISO 1183
Moisture Absorption	0.140 %	0.140 %	23°C / 50% RH; ISO 62
Water Absorption at Saturation	0.42 %	0.42 %	ISO 62
Linear Mold Shrinkage, Flow	0.0050 - 0.0060 cm/cm @Thickness 3.20 mm	0.0050 - 0.0060 in/in @Thickness 0.126 in	SABIC Method
Melt Flow	11 g/10 min @Load 5.00 kg, Temperature 266 °C	11 g/10 min @Load 11.0 lb, Temperature 511 °F	ASTM D1238
Melt Index of Compound	10 g/10 min @Load 5.00 kg, Temperature 265 °C	10 g/10 min @Load 11.0 lb, Temperature 509 °F	MVR [cm^3/10 min]; ISO 1133

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	50.0 MPa	7250 psi	Type I, 5 mm/min; ASTM D638
	50.0 MPa	7250 psi	5 mm/min; ISO 527
Tensile Strength, Yield	55.0 MPa	7980 psi	Type I, 5 mm/min; ASTM D638
	56.0 MPa	8120 psi	5 mm/min; ISO 527
Elongation at Break	8.0 %	8.0 %	5 mm/min; ISO 527
	10 %	10 %	Type I, 5 mm/min; ASTM D638
Elongation at Yield	3.2 %	3.2 %	Type I, 5 mm/min; ASTM D638
	3.2 %	3.2 %	5 mm/min; ISO 527
Tensile Modulus	4.30 GPa	624 ksi	1 mm/min; ISO 527
	4.40 GPa	638 ksi	5 mm/min; ASTM D638
Flexural Yield Strength	90.0 MPa	13100 psi	1.3 mm/min, 50 mm span; ASTM D790
	90.0 MPa	13100 psi	2 mm/min; ISO 178
Flexural Modulus	4.20 GPa	609 ksi	1.3 mm/min, 50 mm span; ASTM D790
	4.20 GPa	609 ksi	2 mm/min; ISO 178
Izod Impact, Notched	0.800 J/cm	1.50 ft-lb/in	ASTM D256
	0.600 J/cm @Temperature -30.0 °C	1.12 ft-lb/in @Temperature -22.0 °F	ASTM D256
Izod Impact, Notched (ISO)	8.00 kJ/m²	3.81 ft-lb/in²	80104; ISO 180/1A
	6.00 kJ/m² @Temperature -30.0 °C	2.86 ft-lb/in² @Temperature -22.0 °F	80104; ISO 180/1A
Izod Impact, Unnotched (ISO)	100 kJ/m²	47.6 ft-lb/in²	80104; ISO 180/1U
	80.0 kJ/m² @Temperature -30.0 °C	38.1 ft-lb/in² @Temperature -22.0 °F	80104; ISO 180/1U
Charpy Impact, Notched	0.600 J/cm²	2.86 ft-lb/in²	Edgew 80104 sp=62mm; ISO 179/1eA
Dart Drop, Total Energy	45.0 J @Temperature 23.0 °C	33.2 ft-lb @Temperature 73.4 °F	ASTM D3763

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	43.0 µm/m-°C @Temperature -40.0 - 40.0 °C	23.9 µin/in-°F @Temperature -40.0 - 104 °F	ASTM E 831
	48.0 µm/m-°C @Temperature -30.0 - 80.0 °C	26.7 µin/in-°F @Temperature -22.0 - 176 °F	ISO 11359-2
	48.0 µm/m-°C @Temperature 23.0 - 80.0 °C	26.7 µin/in-°F @Temperature 73.4 - 176 °F	ISO 11359-2
CTE, linear, Transverse to Flow	64.0 µm/m-°C @Temperature -40.0 - 40.0 °C	35.6 µin/in-°F @Temperature -40.0 - 104 °F	ASTM E 831
	68.0 µm/m-°C @Temperature -30.0 - 80.0 °C	37.8 µin/in-°F @Temperature -22.0 - 176 °F	ISO 11359-2
	68.0 µm/m-°C @Temperature 23.0 - 80.0 °C	37.8 µin/in-°F @Temperature 73.4 - 176 °F	ISO 11359-2
Deflection Temperature at 1.8 MPa (264 psi)	112 °C	234 °F	Flatw 80104 sp=64mm; ISO 75/Af
	112 °C @Thickness 3.20 mm	234 °F @Thickness 0.126 in	unannealed; ASTM D648
Vicat Softening Point	138 °C	280 °F	Rate B/50; ASTM D1525
	138 °C	280 °F	Rate B/50; ISO 306
	140 °C	284 °F	Rate B/120; ISO 306