SABIC Innovative Plastics Xenoy® IQNH2900 PBT+PC (Asia Pacific)
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate/Polybutylene Terephthalate (PBT) Blend, Unreinforced , Polyester, TP , Polybutylene Terephthalate (PBT) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Xenoy® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics Xenoy® IQNH2900 PBT+PC (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
UL94 V-0 Performance with Non-Brominated Flame Retardant. PCR% is up to 12% by using Valox iQ* resin.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.20 g/cc | 1.20 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm |
0.0050 - 0.0070 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Flow | 26 g/10 min @Load 5.00 kg, Temperature 266 °C |
26 g/10 min @Load 11.0 lb, Temperature 511 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 42.0 MPa | 6090 psi | Type I, 50 mm/min; ASTM D638 |
| Tensile Strength, Yield | 63.0 MPa | 9140 psi | Type I, 50 mm/min; ASTM D638 |
| Elongation at Break | 65 % | 65 % | Type I, 50 mm/min; ASTM D638 |
| Elongation at Yield | 4.0 % | 4.0 % | Type I, 50 mm/min; ASTM D638 |
| Tensile Modulus | 2.48 GPa | 360 ksi | 50 mm/min; ASTM D638 |
| Flexural Yield Strength | 89.0 MPa | 12900 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 2.24 GPa | 325 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Izod Impact, Notched | 5.50 J/cm | 10.3 ft-lb/in | ASTM D256 |
| Dart Drop, Total Energy | 65.0 J @Temperature 23.0 °C |
47.9 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 77.0 °C @Thickness 3.20 mm |
171 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Vicat Softening Point | 100 °C | 212 °F | Rate B/50; ASTM D1525 |
| Flammability, UL94 | V-1 @Thickness 1.10 mm |
V-1 @Thickness 0.0433 in |
UL 94 |
| V-0 @Thickness 1.50 mm |
V-0 @Thickness 0.0591 in |
UL 94 | |
| 5VB @Thickness 2.50 mm |
5VB @Thickness 0.0984 in |
UL 94 |