SABIC Innovative Plastics Valox® V3004 PBT (Asia Pacific)

Category Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name Valox®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics Valox® V3004 PBT (Asia Pacific).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Unfilled PBT modified with elastomer. Targeted for flexible hinge, automotive connectors, film applications.
Physical Properties Metric English Comments
Specific Gravity 1.29 g/cc
1.29 g/cc
ASTM D792
Density 1.29 g/cc
0.0466 lb/in³
ISO 1183
Moisture Absorption 0.0800 %
0.0800 %
23°C / 50% RH; ISO 62
Water Absorption at Saturation 0.20 %
0.20 %
ISO 62
Linear Mold Shrinkage, Flow 0.021 - 0.027 cm/cm

@Thickness 3.20 mm
 0.021 - 0.027 in/in

@Thickness 0.126 in
 SABIC Method
Linear Mold Shrinkage, Transverse 0.021 - 0.027 cm/cm

@Thickness 3.20 mm
 0.021 - 0.027 in/in

@Thickness 0.126 in
 SABIC Method
Melt Flow 23 g/10 min

@Load 2.16 kg,
Temperature 250 °C
 23 g/10 min

@Load 4.76 lb,
Temperature 482 °F
 ASTM D1238
Melt Index of Compound 21 g/10 min

@Load 2.16 kg,
Temperature 250 °C
 21 g/10 min

@Load 4.76 lb,
Temperature 482 °F
 MVR [cm^3/10 min]; ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break 22.0 MPa
3190 psi
Type I, 50 mm/min; ASTM D638
30.0 MPa
4350 psi
50 mm/min; ISO 527
Tensile Strength, Yield 50.0 MPa
7250 psi
50 mm/min; ISO 527
51.0 MPa
7400 psi
Type I, 50 mm/min; ASTM D638
Elongation at Break 200 %
200 %
50 mm/min; ISO 527
300 %
300 %
Type I, 50 mm/min; ASTM D638
Elongation at Yield 3.7 %
3.7 %
50 mm/min; ISO 527
4.0 %
4.0 %
Type I, 50 mm/min; ASTM D638
Tensile Modulus 2.35 GPa
341 ksi
1 mm/min; ISO 527
2.40 GPa
348 ksi
50 mm/min; ASTM D638
Flexural Yield Strength 74.0 MPa
10700 psi
2 mm/min; ISO 178
82.0 MPa
11900 psi
1.3 mm/min, 50 mm span; ASTM D790
Flexural Modulus 2.10 GPa
305 ksi
2 mm/min; ISO 178
2.30 GPa
334 ksi
1.3 mm/min, 50 mm span; ASTM D790
Izod Impact, Notched 0.510 J/cm
0.955 ft-lb/in
ASTM D256
0.450 J/cm

@Temperature -30.0 °C
 0.843 ft-lb/in

@Temperature -22.0 °F
 ASTM D256
Izod Impact, Notched (ISO) 6.00 kJ/m²
2.86 ft-lb/in²
80*10*4; ISO 180/1A
4.00 kJ/m²

@Temperature -30.0 °C
 1.90 ft-lb/in²

@Temperature -22.0 °F
 80*10*4; ISO 180/1A
Charpy Impact, Notched 0.700 J/cm²
3.33 ft-lb/in²
Edgew 80*10*4 sp=62mm; ISO 179/1eA
Dart Drop, Total Energy 60.0 J

@Temperature 23.0 °C
 44.3 ft-lb

@Temperature 73.4 °F
 ASTM D3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 91.8 µm/m-°C

@Temperature -40.0 - 40.0 °C
 51.0 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM E 831
91.8 µm/m-°C

@Temperature -40.0 - 40.0 °C
 51.0 µin/in-°F

@Temperature -40.0 - 104 °F
 ISO 11359-2
CTE, linear, Transverse to Flow 75.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
 41.7 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM E 831
75.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
 41.7 µin/in-°F

@Temperature -40.0 - 104 °F
 ISO 11359-2
Deflection Temperature at 0.46 MPa (66 psi) 120 °C

@Thickness 3.20 mm
 248 °F

@Thickness 0.126 in
 unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 48.0 °C
118 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
52.0 °C

@Thickness 3.20 mm
 126 °F

@Thickness 0.126 in
 unannealed; ASTM D648
Vicat Softening Point 110 °C
230 °F
Rate B/50; ISO 306
167 °C
333 °F
Rate B/50; ASTM D1525
170 °C
338 °F
Rate B/120; ISO 306