SABIC Innovative Plastics Valox® V2000DM PBT (Europe-Africa-Middle East)
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Valox® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics Valox® V2000DM PBT (Europe-Africa-Middle East).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Unreinforced, directly metallizable PBT injection molding resin with high flow better release characteristics.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.32 g/cc | 1.32 g/cc | ASTM D792 |
| Density | 1.32 g/cc | 0.0477 lb/in³ | ISO 1183 |
| Moisture Absorption | 0.340 % | 0.340 % | 23°C / 50% RH; ISO 62 |
| Water Absorption at Saturation | 0.080 % | 0.080 % | ISO 62 |
| Linear Mold Shrinkage, Flow | 0.021 - 0.024 cm/cm @Thickness 3.20 mm |
0.021 - 0.024 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Flow | 35.4 g/10 min @Load 2.16 kg, Temperature 250 °C |
35.4 g/10 min @Load 4.76 lb, Temperature 482 °F |
ASTM D1238 |
| Melt Index of Compound | 34 g/10 min @Load 2.16 kg, Temperature 250 °C |
34 g/10 min @Load 4.76 lb, Temperature 482 °F |
MVR [cm^3/10 min]; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 40.0 MPa | 5800 psi | Type I, 50 mm/min; ASTM D638 |
| 55.0 MPa | 7980 psi | 50 mm/min; ISO 527 | |
| Tensile Strength, Yield | 59.0 MPa | 8560 psi | Type I, 50 mm/min; ASTM D638 |
| 59.0 MPa | 8560 psi | 50 mm/min; ISO 527 | |
| Elongation at Break | 15 % | 15 % | 50 mm/min; ISO 527 |
| 100 % | 100 % | Type I, 50 mm/min; ASTM D638 | |
| Elongation at Yield | 7.0 % | 7.0 % | 50 mm/min; ISO 527 |
| 20 % | 20 % | Type I, 50 mm/min; ASTM D638 | |
| Tensile Modulus | 2.60 GPa | 377 ksi | 1 mm/min; ISO 527 |
| 2.80 GPa | 406 ksi | 5 mm/min; ASTM D638 | |
| Flexural Yield Strength | 90.0 MPa | 13100 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 2.50 GPa | 363 ksi | 2 mm/min; ISO 178 |
| 2.57 GPa | 373 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 0.460 J/cm | 0.862 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | NB @Temperature -30.0 °C |
NB @Temperature -22.0 °F |
ASTM D4812 |
| Izod Impact, Notched (ISO) | 5.00 kJ/m² | 2.38 ft-lb/in² | 80*10*4; ISO 180/1A |
| 2.00 kJ/m² @Temperature -30.0 °C |
0.952 ft-lb/in² @Temperature -22.0 °F |
80*10*4; ISO 180/1A | |
| Charpy Impact, Notched | 0.500 J/cm² | 2.38 ft-lb/in² | Edgew 80*10*4 sp=62mm; ISO 179/1eA |
| Dart Drop, Total Energy | 54.0 J @Temperature 23.0 °C |
39.8 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 84.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
46.7 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 84.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
46.7 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 80.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
44.4 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 80.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
44.4 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 53.0 °C | 127 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 54.0 °C @Thickness 3.20 mm |
129 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Vicat Softening Point | 185 °C | 365 °F | Rate B/50; ASTM D1525 |
| 185 °C | 365 °F | Rate B/120; ISO 306 | |
| 186 °C | 367 °F | Rate B/50; ISO 306 |
Users viewing this material also viewed the following:
- Nabaltec NABALOX® NO 105 Calcined Aluminum Oxide
- SABIC Innovative Plastics Lexan® EXL9330S PC Copolymer (Europe-Africa-Middle East)
- Kolon ELLAS K-470A Ester Based Thermoplastic Polyurethane
- Sylvin Technologies 8925-85 Natural PVC Extrusion Compound
- Taiwan Sheen Soon Sheenthane® A8510H TPU for Ink
- UBE 1022T Nylon 6 Monofilament (Drawing Ratio=4.8)
- A. Schulman POLYFORT™ FXP 1227U UV Stable Copolymer Polypropylene
- China Tungsten YT758 Tungsten Carbide
- Braskem TI4020N Impact Copolymer Polypropylene
- 3M 9019 Double Coated Tapes with Adhesive 300
Copyright © lookpolymers.com All Rights Reserved