SABIC Innovative Plastics Valox® SHF436HR PBT

Category Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name Valox®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics Valox® SHF436HR PBT.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
PBT, Super High Flow, 30% glass reinforced,hydrolytically resistant.
Physical Properties Metric English Comments
Specific Gravity 1.53 g/cc
1.53 g/cc
ASTM D792
Density 1.53 g/cc
0.0553 lb/in³
ISO 1183
Moisture Absorption 0.0600 %
0.0600 %
23°C / 50% RH; ISO 62
Water Absorption at Saturation 0.28 %
0.28 %
ISO 62
Linear Mold Shrinkage, Flow 0.0030 - 0.0050 cm/cm

@Thickness 3.20 mm
0.0030 - 0.0050 in/in

@Thickness 0.126 in
SABIC Method
Melt Flow 30 g/10 min

@Load 2.16 kg,
Temperature 250 °C
30 g/10 min

@Load 4.76 lb,
Temperature 482 °F
ASTM D1238
Melt Index of Compound 30 g/10 min

@Load 2.16 kg,
Temperature 250 °C
30 g/10 min

@Load 4.76 lb,
Temperature 482 °F
MVR [cm^3/10 min]; ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break 111 MPa
16100 psi
Type I, 5 mm/min; ASTM D638
117 MPa
17000 psi
5 mm/min; ISO 527
Tensile Strength, Yield 111 MPa
16100 psi
Type I, 5 mm/min; ASTM D638
117 MPa
17000 psi
5 mm/min; ISO 527
Elongation at Break 2.0 %
2.0 %
Type I, 5 mm/min; ASTM D638
2.0 %
2.0 %
5 mm/min; ISO 527
Elongation at Yield 2.0 %
2.0 %
Type I, 5 mm/min; ASTM D638
2.0 %
2.0 %
5 mm/min; ISO 527
Tensile Modulus 9.49 GPa
1380 ksi
1 mm/min; ISO 527
11.9 GPa
1730 ksi
5 mm/min; ASTM D638
Flexural Yield Strength 163 MPa
23600 psi
1.3 mm/min, 50 mm span; ASTM D790
165 MPa
23900 psi
2 mm/min; ISO 178
Flexural Modulus 7.72 GPa
1120 ksi
2 mm/min; ISO 178
8.70 GPa
1260 ksi
1.3 mm/min, 50 mm span; ASTM D790
Izod Impact, Notched 0.920 J/cm
1.72 ft-lb/in
ASTM D256
0.950 J/cm

@Temperature -30.0 °C
1.78 ft-lb/in

@Temperature -22.0 °F
ASTM D256
Izod Impact, Notched (ISO) 8.00 kJ/m²
3.81 ft-lb/in²
80*10*4; ISO 180/1A
8.00 kJ/m²

@Temperature -30.0 °C
3.81 ft-lb/in²

@Temperature -22.0 °F
80*10*4; ISO 180/1A
Charpy Impact, Notched 0.800 J/cm²
3.81 ft-lb/in²
Edgew 80*10*4 sp=62mm; ISO 179/1eA
Dart Drop, Total Energy 6.00 J

@Temperature 23.0 °C
4.43 ft-lb

@Temperature 73.4 °F
ASTM D3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 100 µm/m-°C

@Temperature -40.0 - 40.0 °C
55.6 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
100 µm/m-°C

@Temperature -40.0 - 40.0 °C
55.6 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
CTE, linear, Transverse to Flow 30.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
16.7 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
30.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
16.7 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
Deflection Temperature at 1.8 MPa (264 psi) 206 °C
403 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
214 °C

@Thickness 3.20 mm
417 °F

@Thickness 0.126 in
unannealed; ASTM D648
Vicat Softening Point 200 °C
392 °F
Rate B/50; ASTM D1525
200 °C
392 °F
Rate B/50; ISO 306
200 °C
392 °F
Rate B/120; ISO 306