SABIC Innovative Plastics Valox® HX3091HP PBT

Category Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name Valox®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics Valox® HX3091HP PBT.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
PBT for compounding/fibers only. Not intended for injection molding. Biocompatible. Melt viscosity at 250C and 21.6kgf is 3500-4500 poise. Available in Natural color (1001) only.
Physical Properties Metric English Comments
Specific Gravity 1.31 g/cc
1.31 g/cc
ASTM D792
Density 1.31 g/cc
0.0473 lb/in³
ISO 1183
Moisture Absorption 0.0800 %
0.0800 %
23°C / 50% RH; ISO 62
Water Absorption at Saturation 0.34 %
0.34 %
ISO 62
Viscosity 400000 cP
400000 cP
Melt Viscosity; SABIC Method
Linear Mold Shrinkage, Flow 0.018 - 0.022 cm/cm

@Thickness 3.20 mm
 0.018 - 0.022 in/in

@Thickness 0.126 in
 SABIC Method
Linear Mold Shrinkage, Transverse 0.018 - 0.022 cm/cm

@Thickness 3.20 mm
 0.018 - 0.022 in/in

@Thickness 0.126 in
 SABIC Method
Melt Flow 21 g/10 min

@Load 2.16 kg,
Temperature 250 °C
 21 g/10 min

@Load 4.76 lb,
Temperature 482 °F
 ASTM D1238
Melt Index of Compound 19 g/10 min

@Load 2.16 kg,
Temperature 250 °C
 19 g/10 min

@Load 4.76 lb,
Temperature 482 °F
 MVR [cm^3/10 min]; ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break 30.0 MPa
4350 psi
Type I, 50 mm/min; ASTM D638
45.0 MPa
6530 psi
50 mm/min; ISO 527
Tensile Strength, Yield 46.0 MPa
6670 psi
50 mm/min; ISO 527
56.0 MPa
8120 psi
Type I, 50 mm/min; ASTM D638
Elongation at Break 60 %
60 %
50 mm/min; ISO 527
300 %
300 %
Type I, 50 mm/min; ASTM D638
Elongation at Yield 3.0 %
3.0 %
50 mm/min; ISO 527
3.6 %
3.6 %
Type I, 50 mm/min; ASTM D638
Tensile Modulus 2.50 GPa
363 ksi
1 mm/min; ISO 527
2.53 GPa
367 ksi
5 mm/min; ASTM D638
Flexural Yield Strength 77.0 MPa
11200 psi
1.3 mm/min, 50 mm span; ASTM D790
77.0 MPa
11200 psi
2 mm/min; ISO 178
Flexural Modulus 2.15 GPa
312 ksi
2 mm/min; ISO 178
2.40 GPa
348 ksi
1.3 mm/min, 50 mm span; ASTM D790
Izod Impact, Notched 0.550 J/cm
1.03 ft-lb/in
ASTM D256
0.500 J/cm

@Temperature -30.0 °C
 0.937 ft-lb/in

@Temperature -22.0 °F
 ASTM D256
Izod Impact, Notched (ISO) 5.00 kJ/m²
2.38 ft-lb/in²
80*10*4; ISO 180/1A
5.00 kJ/m²

@Temperature -30.0 °C
 2.38 ft-lb/in²

@Temperature -22.0 °F
 80*10*4; ISO 180/1A
Charpy Impact, Notched 0.800 J/cm²
3.81 ft-lb/in²
Edgew 80*10*4 sp=62mm; ISO 179/1eA
Dart Drop, Total Energy 35.0 J

@Temperature 23.0 °C
 25.8 ft-lb

@Temperature 73.4 °F
 ASTM D3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 77.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
 42.8 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM E 831
77.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
 42.8 µin/in-°F

@Temperature -40.0 - 104 °F
 ISO 11359-2
CTE, linear, Transverse to Flow 80.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
 44.4 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM E 831
80.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
 44.4 µin/in-°F

@Temperature -40.0 - 104 °F
 ISO 11359-2
Deflection Temperature at 0.46 MPa (66 psi) 112 °C

@Thickness 3.20 mm
 234 °F

@Thickness 0.126 in
 unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 50.0 °C
122 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
49.0 °C

@Thickness 3.20 mm
 120 °F

@Thickness 0.126 in
 unannealed; ASTM D648
Vicat Softening Point 170 °C
338 °F
Rate B/50; ASTM D1525
170 °C
338 °F
Rate B/50; ISO 306
171 °C
340 °F
Rate B/120; ISO 306