SABIC Innovative Plastics Valox® FR1 Polybutylene Terephthalate Film, Flame Retardant
| Category | Polymer , Film , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), Flame Retardant |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Valox® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics Valox® FR1 Polybutylene Terephthalate Film, Flame Retardant.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Valox FR-1 film is a flame retardant thermoplastic polybutylene, terephthalite film offering UL94 VTM-0 performance down to 125 microns and good temperature performance. Valox FR-1 film’s outstanding dielectric strength and ease of fabrication (ie: thermoforming, embossing, clean-edge die- cutting, folding and bending) makes it very suitable for a wide range of electrical, electronic and medical applications.Information provided by SABIC Innovative Plastics
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.34 g/cc | 0.0484 lb/in³ | ASTM D792 |
| Water Absorption | 0.48 % | 0.48 % | 24 hrs; ASTM D570 |
| Surface Tension | 34 - 36 dynes/cm | 34 - 36 dynes/cm | 2nd surface; units: Dyne; Dyne Pens |
| >= 44 dynes/cm | >= 44 dynes/cm | 1st surface; units: Dyne; Dyne Pens |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 41.4 MPa | 6000 psi | ASTM D882 |
| Tensile Strength, Yield | 49.6 MPa | 7190 psi | ASTM D882 |
| Elongation at Break | 57 % | 57 % | ASTM D882 |
| Tensile Modulus | 1.91 GPa | 277 ksi | ASTM D882 |
| Gardner Impact | 9.49 J @Thickness 0.762 mm |
7.00 ft-lb @Thickness 0.0300 in |
ASTM D3029 |
| Impact Test | 12.2 J | 9.00 ft-lb | Puncture Resistance, Dynatup; ASTM D3763 |
| Tear Strength | 39.8 kN/m | 227 pli | propogation; ASTM D1922 |
| 256 kN/m | 1460 pli | initiation; ASTM D1004 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 55.8 µm/m-°C | 31.0 µin/in-°F | ASTM E831 |
| Specific Heat Capacity | 1.26 J/g-°C | 0.301 BTU/lb-°F | ASTM E1269 |
| Thermal Conductivity | 0.200 W/m-K | 1.39 BTU-in/hr-ft²-°F | ASTM D5470 |
| Deflection Temperature at 1.8 MPa (264 psi) | 78.9 °C | 174 °F | TMA |
| Vicat Softening Point | 174.4 °C | 345.9 °F | ASTM 1525-00 modified |
| Brittleness Temperature | -135 °C | -211 °F | ASTM D746 |
| Glass Transition Temp, Tg | 28.8 °C | 83.9 °F | ASTM D3417/D3418 |
| Flammability, UL94 | V-2 @Thickness 0.0750 - 0.130 mm |
V-2 @Thickness 0.00295 - 0.00512 in |
VTM |
| V-0 @Thickness 0.130 - 0.250 mm |
V-0 @Thickness 0.00512 - 0.00984 in |
VTM | |
| V-0 @Thickness 0.500 - 0.625 mm |
V-0 @Thickness 0.0197 - 0.0246 in |
VTM | |
| V-0 @Thickness >=0.625 mm |
V-0 @Thickness >=0.0246 in |
||
| Shrinkage | 0.40 % @Temperature 150 °C |
0.40 % @Temperature 302 °F |
ASTM D1204 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Gloss | 5.0 % | 5.0 % | over Flat Black min/max @ 60º; ASTM D523-60 |
| 0.10 - 17 % | 0.10 - 17 % | Matte @ 85º; ASTM D523-85 | |
| 0.10 - 25 % | 0.10 - 25 % | Matte @ 85º; ASTM D523-85 | |
| Yellow Index | 49 % | 49 % | ASTM D1925 |
| Transmission, Visible | 15 % | 15 % | ASTM D1003 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+17 ohm-cm | 1.00e+17 ohm-cm | ASTM D257 |
| Surface Resistivity per Square | 1.00e+16 ohm | 1.00e+16 ohm | ASTM D257 |
| Dielectric Constant | 2.8 @Frequency 1.00e+6 Hz |
2.8 @Frequency 1.00e+6 Hz |
ASTM D150 |
| 3.3 @Frequency 60.0 Hz |
3.3 @Frequency 60.0 Hz |
ASTM D150 | |
| Dielectric Strength | 42.9 kV/mm @Temperature 23.0 °C |
1090 kV/in @Temperature 73.4 °F |
in oil, short time. 0.25mm; ASTM D149-97a Method A |
| Dissipation Factor | 0.0015 @Frequency 60.0 Hz |
0.0015 @Frequency 60.0 Hz |
ASTM D150 |
| 0.010 @Frequency 1.00e+6 Hz |
0.010 @Frequency 1.00e+6 Hz |
ASTM D150 | |
| Arc Resistance | 21 sec | 21 sec | Tungsten; ASTM D495 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Fold Endurance (folds) | 2000 | MIT; ASTM D2176-69; double, 0.175mm |
| 83 | MIT; ASTM D2176-69; double, 0.625mm | |
| Nominal Gauge Variation (%) | 10 | 0.075 - 0.250mm |
| 5 | 0.375 - 0.750mm | |
| Pencil Hardness | 2B-B | |
| Surface Energy | 35 | 2nd surface; ASTM D5946-01 |
| 36 | 1st surface; ASTM D5946-01 |