SABIC Innovative Plastics Valox® 364 PBT (Asia Pacific)
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Valox® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics Valox® 364 PBT (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Designed for outdoor telecommunications enclosure applications.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.31 g/cc | 1.31 g/cc | ASTM D792 |
| Density | 1.31 g/cc | 0.0473 lb/in³ | ISO 1183 |
| Moisture Absorption | 0.0300 % | 0.0300 % | 23°C / 50% RH; ISO 62 |
| Water Absorption at Saturation | 0.090 % | 0.090 % | ISO 62 |
| Linear Mold Shrinkage, Flow | 0.010 cm/cm @Thickness 3.20 mm |
0.010 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Flow | 19 g/10 min @Load 5.00 kg, Temperature 266 °C |
19 g/10 min @Load 11.0 lb, Temperature 511 °F |
ASTM D1238 |
| Melt Index of Compound | 17 g/10 min @Load 5.00 kg, Temperature 265 °C |
17 g/10 min @Load 11.0 lb, Temperature 509 °F |
MVR [cm^3/10 min]; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 36.0 MPa | 5220 psi | Type I, 50 mm/min; ASTM D638 |
| 36.0 MPa | 5220 psi | 50 mm/min; ISO 527 | |
| Tensile Strength, Yield | 45.0 MPa | 6530 psi | Type I, 50 mm/min; ASTM D638 |
| 46.0 MPa | 6670 psi | 50 mm/min; ISO 527 | |
| Elongation at Break | 36 % | 36 % | 50 mm/min; ISO 527 |
| 39 % | 39 % | Type I, 50 mm/min; ASTM D638 | |
| Elongation at Yield | 4.0 % | 4.0 % | Type I, 50 mm/min; ASTM D638 |
| 4.0 % | 4.0 % | 50 mm/min; ISO 527 | |
| Tensile Modulus | 1.95 GPa | 283 ksi | 1 mm/min; ISO 527 |
| 1.96 GPa | 284 ksi | 5 mm/min; ASTM D638 | |
| Flexural Yield Strength | 67.0 MPa | 9720 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 69.0 MPa | 10000 psi | 2 mm/min; ISO 178 | |
| Flexural Modulus | 1.77 GPa | 257 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 1.83 GPa | 265 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 7.17 J/cm | 13.4 ft-lb/in | ASTM D256 |
| 4.27 J/cm @Temperature -40.0 °C |
8.00 ft-lb/in @Temperature -40.0 °F |
ASTM D256 | |
| 6.94 J/cm @Temperature -20.0 °C |
13.0 ft-lb/in @Temperature -4.00 °F |
ASTM D256 | |
| Izod Impact, Notched (ISO) | 51.0 kJ/m² | 24.3 ft-lb/in² | 80*10*4; ISO 180/1A |
| 17.0 kJ/m² @Temperature -30.0 °C |
8.09 ft-lb/in² @Temperature -22.0 °F |
80*10*4; ISO 180/1A | |
| Charpy Impact, Notched | 5.10 J/cm² | 24.3 ft-lb/in² | Edgew 80*10*4 sp=62mm; ISO 179/1eA |
| Dart Drop, Total Energy | 45.0 J @Temperature -20.0 °C |
33.2 ft-lb @Temperature -4.00 °F |
ASTM D3763 |
| 47.0 J @Temperature -40.0 °C |
34.7 ft-lb @Temperature -40.0 °F |
ASTM D3763 | |
| 47.0 J @Temperature 23.0 °C |
34.7 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 95.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
52.8 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 95.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
52.8 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 98.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
54.4 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 100 µm/m-°C @Temperature -40.0 - 40.0 °C |
55.6 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 103 °C @Thickness 3.20 mm |
217 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 74.0 °C | 165 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 65.0 °C @Thickness 3.20 mm |
149 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Vicat Softening Point | 115 °C | 239 °F | Rate B/50; ASTM D1525 |
| 119 °C | 246 °F | Rate B/50; ISO 306 | |
| 122 °C | 252 °F | Rate B/120; ISO 306 | |
| UL RTI, Electrical | 75.0 °C | 167 °F | UL 746B |
| UL RTI, Mechanical with Impact | 75.0 °C | 167 °F | UL 746B |
| UL RTI, Mechanical without Impact | 75.0 °C | 167 °F | UL 746B |
| Flammability, UL94 | V-0 @Thickness 1.47 mm |
V-0 @Thickness 0.0579 in |
UL 94 |
| 5VA @Thickness 2.99 mm |
5VA @Thickness 0.118 in |
UL 94 | |
| Oxygen Index | 28 % | 28 % | ASTM D2863 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Arc Resistance | 120 - 180 sec | 120 - 180 sec | Tungsten; ASTM D495 |
| Comparative Tracking Index | >= 600 V | >= 600 V | UL 746A |
| Hot Wire Ignition, HWI | 30 - 60 sec | 30 - 60 sec | UL 746A |
| High Amp Arc Ignition, HAI | >= 120 arcs | >= 120 arcs | UL 746A |
| High Voltage Arc-Tracking Rate, HVTR | 25.4 - 80.0 mm/min | 1.00 - 3.15 in/min | UL 746A |
| Descriptive Properties | Value | Comments |
|---|---|---|
| UV-light, water exposure/immersion | F2 | UL 746C |
Users viewing this material also viewed the following:
- Industrial Laminates/Norplex NP611 Paper Base Laminate
- Michelman® Michem® Emulsion 62330 Anionic paraffin/polyethylene emulsion
- Iran Petrochemical (PCC) SBR-1712 Styrene Butadiene Rubber
- Lucite International Colacryl ® TS1875 Acrylic Solution Resin
- Karina E 800-10/1-AY-RT PVC Compound White Color
- Kazanorgsintez 108-278 Low Density Polyethylene Composition with Improved Processibility
- ExxonMobil Diol 17 RD 40
- TSE Industries Millathane® 5004 Millable Polyurethane Elastomer, 350ºF Cure Temperature
- ChevronTexaco FM ISO 46 Synthetic Compressor Oil
- BASF Styropor® BFL 322 EPS