SABIC Innovative Plastics Ultem HATX200 PEI+PCE (Asia Pacific)

Category Polymer , Thermoplastic , Polyetherimide (PEI) , Polyetherimide (PEI) + PCE
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name ULTEM
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics Ultem HATX200 PEI+PCE (Asia Pacific).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
High flow Polyetherimide blend. ECO Conforming. For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible (ISO 10993 or USP Class VI), food contact compliant.This data was supplied by SABIC-IP for the Asia Pacific region.
Physical Properties Metric English Comments
Specific Gravity 1.26 g/cc
1.26 g/cc
ASTM D 792
Density 1.27 g/cc
0.0459 lb/in³
ISO 1183
Moisture Absorption at Equilibrium 0.50 %
0.50 %
23°C / 50% RH; ISO 62
Water Absorption at Saturation 0.90 %

@Temperature 23.0 °C
0.90 %

@Temperature 73.4 °F
ISO 62
Linear Mold Shrinkage, Flow 0.0050 - 0.0070 cm/cm

@Thickness 3.20 mm
0.0050 - 0.0070 in/in

@Thickness 0.126 in
SABIC Method
Melt Flow 16 g/10 min

@Load 5.00 kg,
Temperature 220 °C
16 g/10 min

@Load 11.0 lb,
Temperature 428 °F
[cm^3/10 min] Melt Volume Rate; ISO 1133
24 g/10 min

@Load 6.60 kg,
Temperature 337 °C
24 g/10 min

@Load 14.6 lb,
Temperature 639 °F
ASTM D 1238
Mechanical Properties Metric English Comments
Tensile Strength at Break 75.0 MPa
10900 psi
Type I, 5 mm/min; ASTM D 638
75.0 MPa
10900 psi
5 mm/min; ISO 527
Tensile Strength, Yield 95.0 MPa
13800 psi
5 mm/min; ISO 527
96.0 MPa
13900 psi
Type I, 5 mm/min; ASTM D 638
Elongation at Break 20 %
20 %
5 mm/min; ISO 527
70 %
70 %
Type I, 5 mm/min; ASTM D 638
Elongation at Yield 6.5 %
6.5 %
5 mm/min; ISO 527
30 %
30 %
Type I, 5 mm/min; ASTM D 638
Tensile Modulus 3.00 GPa
435 ksi
5 mm/min; ASTM D 638
3.00 GPa
435 ksi
1 mm/min; ISO 527
Flexural Yield Strength 125 MPa
18100 psi
2 mm/min; ISO 178
144 MPa
20900 psi
1.3 mm/min, 50 mm span; ASTM D 790
Flexural Modulus 3.10 GPa
450 ksi
2 mm/min; ISO 178
3.17 GPa
460 ksi
1.3 mm/min, 50 mm span; ASTM D 790
Izod Impact, Notched 0.530 J/cm

@Temperature 23.0 °C
0.993 ft-lb/in

@Temperature 73.4 °F
ASTM D 256
Izod Impact, Unnotched 20.82 J/cm

@Temperature 23.0 °C
39.00 ft-lb/in

@Temperature 73.4 °F
ASTM D 4812
Izod Impact, Notched (ISO) 5.00 kJ/m²

@Temperature 23.0 °C
2.38 ft-lb/in²

@Temperature 73.4 °F
80*10*4; ISO 180/1A
5.00 kJ/m²

@Temperature -30.0 °C
2.38 ft-lb/in²

@Temperature -22.0 °F
80*10*4; ISO 180/1A
Charpy Impact, Notched 0.400 J/cm²

@Temperature 23.0 °C
1.90 ft-lb/in²

@Temperature 73.4 °F
V-notch Edgew 80*10*4 sp=62mm; ISO 179/1eA
Impact Test 28.0 J

@Temperature 23.0 °C
20.7 ft-lb

@Temperature 73.4 °F
Instrumented Impact Total Energy; ASTM D 3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 60.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
33.3 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
60.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
33.3 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
CTE, linear, Transverse to Flow 60.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
33.3 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
60.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
33.3 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
Deflection Temperature at 1.8 MPa (264 psi) 180 °C
356 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
190 °C

@Thickness 6.40 mm
374 °F

@Thickness 0.252 in
unannealed; ASTM D 648
Vicat Softening Point 205 °C
401 °F
Rate B/120; ISO 306
210 °C
410 °F
Rate B/50; ASTM D 1525
210 °C
410 °F
Rate B/50; ISO 306
Flammability, UL94 V-2

@Thickness 0.760 mm
V-2

@Thickness 0.0299 in
UL 94