SABIC Innovative Plastics Ultem CRS5211 PEI (Asia Pacific)

Category Polymer , Thermoplastic , Polyetherimide (PEI)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name ULTEM
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics Ultem CRS5211 PEI (Asia Pacific).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
20% Glass fiber filled, enhanced flow Polyetherimide copolymer (Tg 225C) with enhanced chemical resistance to strong acids, bases, aromatics, and ketones. ECO Conforming, UL94 V0 and 5VA listing.This data was supplied by SABIC-IP for the Asia Pacific region.
Physical Properties Metric English Comments
Specific Gravity 1.42 g/cc
1.42 g/cc
ASTM D 792
Melt Flow 5.1 g/10 min

@Load 6.60 kg,
Temperature 337 °C
5.1 g/10 min

@Load 14.6 lb,
Temperature 639 °F
ASTM D 1238
Mechanical Properties Metric English Comments
Tensile Strength at Break 137 MPa
19900 psi
Type I, 5 mm/min; ASTM D 638
Elongation at Break 3.0 %
3.0 %
Type I, 5 mm/min; ASTM D 638
Tensile Modulus 6.89 GPa
999 ksi
5 mm/min; ASTM D 638
Flexural Yield Strength 213 MPa
30900 psi
2.6 mm/min, 100 mm span; ASTM D 790
Flexural Modulus 6.89 GPa
999 ksi
2.6 mm/min, 100 mm span; ASTM D 790
Izod Impact, Notched 0.850 J/cm

@Temperature 23.0 °C
1.59 ft-lb/in

@Temperature 73.4 °F
ASTM D 256
4.80 J/cm

@Thickness 3.20 mm
8.99 ft-lb/in

@Thickness 0.126 in
reverse notched; ASTM D 256
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 218 °C

@Thickness 6.40 mm
424 °F

@Thickness 0.252 in
unannealed; ASTM D 648
Glass Transition Temp, Tg 225 °C
437 °F
UL RTI, Electrical 105 °C
221 °F
UL 746B
UL RTI, Mechanical with Impact 105 °C
221 °F
UL 746B
UL RTI, Mechanical without Impact 105 °C
221 °F
UL 746B
Flammability, UL94 V-0

@Thickness 1.47 mm
V-0

@Thickness 0.0579 in
UL 94
5VA

@Thickness 1.47 mm
5VA

@Thickness 0.0579 in
UL 94
Electrical Properties Metric English Comments
Arc Resistance 120 - 180 sec
120 - 180 sec
Tungsten, PLC code 5; ASTM D 495
Comparative Tracking Index 100 - 175 V
100 - 175 V
PLC code 4; UL 746A
Hot Wire Ignition, HWI >= 120 sec
>= 120 sec
PLC code 0; UL 746A
High Amp Arc Ignition, HAI 0.00 - 15 arcs
0.00 - 15 arcs
surface, PLC code 4; UL 746A
High Voltage Arc-Tracking Rate, HVTR 80.0 - 150 mm/min
3.15 - 5.91 in/min
PLC code 3; UL 746A