SABIC Innovative Plastics Ultem 2412EPR PEI (Europe-Africa-Middle East)

Category Polymer , Thermoplastic , Polyetherimide (PEI)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name ULTEM
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics Ultem 2412EPR PEI (Europe-Africa-Middle East).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
40% Milled glass filled, high flow Polyetherimide (Tg 217C) with internal mold release and enhanced electroplatability. ECO Conforming, UL94 V0 listing.This data was supplied by SABIC-IP for the Europe-Africa-Middle East region.
Physical Properties Metric English Comments
Specific Gravity 1.56 g/cc
1.56 g/cc
ASTM D 792
Density 1.56 g/cc
0.0564 lb/in³
ISO 1183
Moisture Absorption at Equilibrium 0.40 %
0.40 %
23°C / 50% RH; ISO 62
Water Absorption at Saturation 0.80 %

@Temperature 23.0 °C
0.80 %

@Temperature 73.4 °F
ISO 62
Linear Mold Shrinkage, Flow 0.0020 - 0.0040 cm/cm
0.0020 - 0.0040 in/in
on tensile bar; SABIC Method
0.0020 - 0.0040 cm/cm

@Thickness 3.20 mm
0.0020 - 0.0040 in/in

@Thickness 0.126 in
SABIC Method
Linear Mold Shrinkage, Transverse 0.0020 - 0.0040 cm/cm

@Thickness 3.20 mm
0.0020 - 0.0040 in/in

@Thickness 0.126 in
SABIC Method
Melt Flow 9.5 g/10 min

@Load 6.60 kg,
Temperature 337 °C
9.5 g/10 min

@Load 14.6 lb,
Temperature 639 °F
ASTM D 1238
13 g/10 min

@Load 5.00 kg,
Temperature 360 °C
13 g/10 min

@Load 11.0 lb,
Temperature 680 °F
[cm^3/10 min] Melt Volume Rate; ISO 1133
Mechanical Properties Metric English Comments
Hardness, H358/30 165 MPa
23900 psi
ISO 2039-1
Tensile Strength at Break 90.0 MPa
13100 psi
5 mm/min; ISO 527
105 MPa
15200 psi
Type I, 5 mm/min; ASTM D 638
Tensile Strength, Yield 90.0 MPa
13100 psi
5 mm/min; ISO 527
105 MPa
15200 psi
Type I, 5 mm/min; ASTM D 638
Elongation at Break 1.5 %
1.5 %
Type I, 5 mm/min; ASTM D 638
2.0 %
2.0 %
5 mm/min; ISO 527
Elongation at Yield 1.5 %
1.5 %
Type I, 5 mm/min; ASTM D 638
2.0 %
2.0 %
5 mm/min; ISO 527
Tensile Modulus 9.80 GPa
1420 ksi
5 mm/min; ASTM D 638
10.1 GPa
1460 ksi
1 mm/min; ISO 527
Flexural Yield Strength 145 MPa
21000 psi
2 mm/min; ISO 178
148 MPa
21500 psi
1.3 mm/min, 50 mm span; ASTM D 790
Flexural Modulus 6.91 GPa
1000 ksi
1.3 mm/min, 50 mm span; ASTM D 790
7.20 GPa
1040 ksi
2 mm/min; ISO 178
Izod Impact, Notched 0.370 J/cm

@Temperature 23.0 °C
0.693 ft-lb/in

@Temperature 73.4 °F
ASTM D 256
Izod Impact, Unnotched 4.43 J/cm

@Temperature 23.0 °C
8.30 ft-lb/in

@Temperature 73.4 °F
ASTM D 4812
Izod Impact, Notched (ISO) 5.00 kJ/m²

@Temperature 23.0 °C
2.38 ft-lb/in²

@Temperature 73.4 °F
80*10*4; ISO 180/1A
5.00 kJ/m²

@Temperature -30.0 °C
2.38 ft-lb/in²

@Temperature -22.0 °F
80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 25.0 kJ/m²

@Temperature 23.0 °C
11.9 ft-lb/in²

@Temperature 73.4 °F
80*10*4; ISO 180/1U
25.0 kJ/m²

@Temperature -30.0 °C
11.9 ft-lb/in²

@Temperature -22.0 °F
80*10*4; ISO 180/1U
Charpy Impact Unnotched 2.00 J/cm²

@Temperature -30.0 °C
9.52 ft-lb/in²

@Temperature -22.0 °F
Edgew 80*10*4 sp=62mm; ISO 179/1eU
2.10 J/cm²

@Temperature 23.0 °C
9.99 ft-lb/in²

@Temperature 73.4 °F
Edgew 80*10*4 sp=62mm; ISO 179/1eU
Charpy Impact, Notched 0.500 J/cm²

@Temperature 23.0 °C
2.38 ft-lb/in²

@Temperature 73.4 °F
V-notch Edgew 80*10*4 sp=62mm; ISO 179/1eA
0.500 J/cm²

@Temperature -30.0 °C
2.38 ft-lb/in²

@Temperature -22.0 °F
V-notch Edgew 80*10*4 sp=62mm; ISO 179/1eA
Impact Test 16.0 J

@Temperature 23.0 °C
11.8 ft-lb

@Temperature 73.4 °F
Instrumented Impact Total Energy; ASTM D 3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 25.0 µm/m-°C

@Temperature -40.0 - 150 °C
13.9 µin/in-°F

@Temperature -40.0 - 302 °F
ASTM E 831
25.0 µm/m-°C

@Temperature 23.0 - 150 °C
13.9 µin/in-°F

@Temperature 73.4 - 302 °F
ISO 11359-2
CTE, linear, Transverse to Flow 30.0 µm/m-°C

@Temperature -40.0 - 150 °C
16.7 µin/in-°F

@Temperature -40.0 - 302 °F
ASTM E 831
30.0 µm/m-°C

@Temperature 23.0 - 150 °C
16.7 µin/in-°F

@Temperature 73.4 - 302 °F
ISO 11359-2
Thermal Conductivity 0.280 W/m-K
1.94 BTU-in/hr-ft²-°F
ISO 8302
Deflection Temperature at 0.46 MPa (66 psi) 206 °C
403 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
207 °C
405 °F
Edgew 120*10*4 sp=100mm; ISO 75/Be
211 °C

@Thickness 3.20 mm
412 °F

@Thickness 0.126 in
unannealed; ASTM D 648
213 °C

@Thickness 6.40 mm
415 °F

@Thickness 0.252 in
unannealed; ASTM D 648
Deflection Temperature at 1.8 MPa (264 psi) 195 °C
383 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
203 °C
397 °F
Edgew 120*10*4 sp=100mm; ISO 75/Ae
202 °C

@Thickness 3.20 mm
396 °F

@Thickness 0.126 in
unannealed; ASTM D 648
203 °C

@Thickness 6.40 mm
397 °F

@Thickness 0.252 in
unannealed; ASTM D 648
Vicat Softening Point 213 °C
415 °F
Rate B/50; ISO 306
214 °C
417 °F
Rate B/120; ISO 306
222 °C
432 °F
Rate B/50; ASTM D 1525
Glass Transition Temp, Tg 217 °C
423 °F
Flammability, UL94 V-0

@Thickness 0.400 mm
V-0

@Thickness 0.0157 in
UL 94
Electrical Properties Metric English Comments
Arc Resistance 120 - 180 sec
120 - 180 sec
Tungsten, PLC code 5; ASTM D 495
Comparative Tracking Index 175 - 250 V
175 - 250 V
PLC code 3; UL 746A
Hot Wire Ignition, HWI 7.0 - 15 sec
7.0 - 15 sec
PLC code 4; UL 746A
High Amp Arc Ignition, HAI 0.00 - 15 arcs
0.00 - 15 arcs
surface, PLC code 4; UL 746A
High Voltage Arc-Tracking Rate, HVTR >= 150 mm/min
>= 5.91 in/min
PLC code 4; UL 746A
Descriptive Properties Value Comments
Ball Pressure Test, 125°C +/- 2°C Passes
IEC 60695-10-2