SABIC Innovative Plastics Ultem 2313 PEI (Asia Pacific)

Category Polymer , Thermoplastic , Polyetherimide (PEI)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name ULTEM
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics Ultem 2313 PEI (Asia Pacific).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
30% Milled glass filled, enhanced flow Polyetherimide (Tg 217C) with enhanced electroplatability. ECO Conforming, UL94 V0 and 5VA listing.This data was supplied by SABIC-IP for the Asia Pacific region.
Physical Properties Metric English Comments
Specific Gravity 1.52 g/cc
1.52 g/cc
ASTM D 792
Water Absorption 0.18 %

@Time 86400 sec
0.18 %

@Time 24.0 hour
ASTM D 570
Moisture Absorption at Equilibrium 0.98 %

@Temperature 23.0 °C
0.98 %

@Temperature 73.4 °F
ASTM D 570
Linear Mold Shrinkage, Flow 0.0030 - 0.0040 cm/cm

@Thickness 3.20 mm
0.0030 - 0.0040 in/in

@Thickness 0.126 in
SABIC Method
Linear Mold Shrinkage, Transverse 0.0045 - 0.0055 cm/cm

@Thickness 3.20 mm
0.0045 - 0.0055 in/in

@Thickness 0.126 in
SABIC Method
Melt Flow 9.3 g/10 min

@Load 6.60 kg,
Temperature 337 °C
9.3 g/10 min

@Load 14.6 lb,
Temperature 639 °F
ASTM D 1238
Mechanical Properties Metric English Comments
Tensile Strength at Break 86.0 MPa
12500 psi
Type I, 5 mm/min; ASTM D 638
Elongation at Break 3.0 %
3.0 %
Type I, 5 mm/min; ASTM D 638
Flexural Strength 172 MPa
24900 psi
2.6 mm/min, 100 mm span; ASTM D 790
Flexural Modulus 6.96 GPa
1010 ksi
2.6 mm/min, 100 mm span; ASTM D 790
Izod Impact, Notched 0.320 J/cm

@Temperature 23.0 °C
0.599 ft-lb/in

@Temperature 73.4 °F
ASTM D 256
2.67 J/cm

@Thickness 3.20 mm
5.00 ft-lb/in

@Thickness 0.126 in
reverse notched; ASTM D 256
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 207 °C

@Thickness 6.40 mm
405 °F

@Thickness 0.252 in
unannealed; ASTM D 648
Glass Transition Temp, Tg 217 °C
423 °F
UL RTI, Electrical 105 °C
221 °F
UL 746B
UL RTI, Mechanical with Impact 105 °C
221 °F
UL 746B
UL RTI, Mechanical without Impact 105 °C
221 °F
UL 746B
Flammability, UL94 V-0

@Thickness 0.350 mm
V-0

@Thickness 0.0138 in
UL 94
Electrical Properties Metric English Comments
Dielectric Constant 3.7

@Frequency 1000 Hz
3.7

@Frequency 1000 Hz
ASTM D 150
Arc Resistance 60 - 120 sec
60 - 120 sec
Tungsten, PLC code 6; ASTM D 495
Comparative Tracking Index 100 - 175 V
100 - 175 V
PLC code 4; UL 746A
Hot Wire Ignition, HWI 60 - 120 sec
60 - 120 sec
PLC code 1; UL 746A
High Amp Arc Ignition, HAI 0.00 - 15 arcs
0.00 - 15 arcs
surface, PLC code 4; UL 746A
High Voltage Arc-Tracking Rate, HVTR 25.4 - 80.0 mm/min
1.00 - 3.15 in/min
PLC code 2; UL 746A