SABIC Innovative Plastics Ultem 2212 PEI (Europe-Africa-Middle East)

Category Polymer , Thermoplastic , Polyetherimide (PEI)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name ULTEM
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics Ultem 2212 PEI (Europe-Africa-Middle East).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
20% Milled glass filled, enhanced flow Polyetherimide (Tg 217C). ECO Conforming, UL94 V0 and 5VA listing.This data was supplied by SABIC-IP for the Europe-Africa-Middle East region.
Physical Properties Metric English Comments
Density 1.43 g/cc
0.0517 lb/in³
ISO 1183
Linear Mold Shrinkage, Flow 0.0030 - 0.0050 cm/cm
0.0030 - 0.0050 in/in
on tensile bar; SABIC Method
Mechanical Properties Metric English Comments
Tensile Strength at Break 75.0 MPa
10900 psi
5 mm/min; ISO 527
Elongation at Break 8.0 %
8.0 %
5 mm/min; ISO 527
Tensile Modulus 4.50 GPa
653 ksi
1 mm/min; ISO 527
Flexural Yield Strength 135 MPa
19600 psi
2 mm/min; ISO 178
Izod Impact, Unnotched (ISO) 30.0 kJ/m²

@Temperature 23.0 °C
14.3 ft-lb/in²

@Temperature 73.4 °F
80*10*4; ISO 180/1U
Thermal Properties Metric English Comments
Thermal Conductivity 0.280 W/m-K
1.94 BTU-in/hr-ft²-°F
ISO 8302
Deflection Temperature at 0.46 MPa (66 psi) 202 °C
396 °F
Edgew 120*10*4 sp=100mm; ISO 75/Be
Deflection Temperature at 1.8 MPa (264 psi) 189 °C
372 °F
Edgew 120*10*4 sp=100mm; ISO 75/Ae
Vicat Softening Point 211 °C
412 °F
Rate B/120; ISO 306
Glass Transition Temp, Tg 217 °C
423 °F
UL RTI, Electrical 170 °C
338 °F
UL 746B
UL RTI, Mechanical with Impact 170 °C
338 °F
UL 746B
UL RTI, Mechanical without Impact 170 °C
338 °F
UL 746B
Flammability, UL94 V-0

@Thickness 0.410 mm
V-0

@Thickness 0.0161 in
UL 94