SABIC Innovative Plastics Ultem 2100N PEI

Category Polymer , Thermoplastic , Polyetherimide (PEI)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name ULTEM
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics Ultem 2100N PEI.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
10% Glass fiber filled, standard flow Polyetherimide (Tg 217C). ECO Conforming.This data was supplied by SABIC-IP for the Americas region.
Physical Properties Metric English Comments
Specific Gravity 1.34 g/cc
1.34 g/cc
ASTM D 792
Water Absorption 0.21 %

@Time 86400 sec
0.21 %

@Time 24.0 hour
ASTM D 570
Moisture Absorption at Equilibrium 1.2 %

@Temperature 23.0 °C
1.2 %

@Temperature 73.4 °F
ASTM D 570
Linear Mold Shrinkage, Flow 0.0050 - 0.0060 cm/cm

@Thickness 3.20 mm
0.0050 - 0.0060 in/in

@Thickness 0.126 in
SABIC Method
Melt Flow 7.0 g/10 min

@Load 6.60 kg,
Temperature 337 °C
7.0 g/10 min

@Load 14.6 lb,
Temperature 639 °F
ASTM D 1238
Mechanical Properties Metric English Comments
Hardness, Rockwell M 114
114
ASTM D 785
Tensile Strength at Break 115 MPa
16700 psi
Type I, 5 mm/min; ASTM D 638
Tensile Strength, Yield 114 MPa
16500 psi
Type I, 5 mm/min; ASTM D 638
Elongation at Break 6.0 %
6.0 %
Type I, 5 mm/min; ASTM D 638
Tensile Modulus 4.68 GPa
679 ksi
5 mm/min; ASTM D 638
Flexural Strength 199 MPa
28900 psi
2.6 mm/min, 100 mm span; ASTM D 790
Flexural Modulus 5.17 GPa
750 ksi
2.6 mm/min, 100 mm span; ASTM D 790
Izod Impact, Notched 0.530 J/cm

@Temperature 23.0 °C
0.993 ft-lb/in

@Temperature 73.4 °F
ASTM D 256
4.59 J/cm

@Thickness 3.20 mm
8.60 ft-lb/in

@Thickness 0.126 in
reverse notched; ASTM D 256
Izod Impact, Unnotched 4.80 J/cm

@Temperature 23.0 °C
8.99 ft-lb/in

@Temperature 73.4 °F
ASTM D 4812
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 32.4 µm/m-°C

@Temperature -20.0 - 150 °C
18.0 µin/in-°F

@Temperature -4.00 - 302 °F
ASTM E 831
Deflection Temperature at 0.46 MPa (66 psi) 210 °C

@Thickness 6.40 mm
410 °F

@Thickness 0.252 in
unannealed; ASTM D 648
Deflection Temperature at 1.8 MPa (264 psi) 208 °C

@Thickness 6.40 mm
406 °F

@Thickness 0.252 in
unannealed; ASTM D 648
Vicat Softening Point 223 °C
433 °F
Rate B/50; ASTM D 1525
Glass Transition Temp, Tg 217 °C
423 °F
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+17 ohm-cm
1.00e+17 ohm-cm
ASTM D 257
Dielectric Constant 3.5

@Frequency 1000 Hz
3.5

@Frequency 1000 Hz
ASTM D 150
Dielectric Strength 27.5 kV/mm

@Thickness 1.60 mm
699 kV/in

@Thickness 0.0630 in
in oil; ASTM D 149
Dissipation Factor 0.0014

@Frequency 1000 Hz
0.0014

@Frequency 1000 Hz
ASTM D 150
0.0046

@Frequency 2.45e+9 Hz
0.0046

@Frequency 2.45e+9 Hz
ASTM D 150