SABIC Innovative Plastics ULTEM XH6050F PEI Copolymer

Category Polymer , Thermoplastic , Polyetherimide (PEI)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name ULTEM
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics ULTEM XH6050F PEI Copolymer.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Transparent, enhanced flow Polyetherimidesulfone copolymer (Tg 247C). ECO Conforming. US FDA Compliant. Resin is subject to U.S. Commerce Control Laws (15CFR Chapter VII, Part 774).
Physical Properties Metric English Comments
Specific Gravity 1.30 g/cc
1.30 g/cc
ASTM D792
Density 1.30 g/cc
0.0470 lb/in³
ISO 1183
Moisture Absorption 0.600 %
0.600 %
23°C / 50% RH; ISO 62
Water Absorption at Saturation 1.75 %
1.75 %
ISO 62
Linear Mold Shrinkage, Flow 0.0050 - 0.0070 cm/cm
0.0050 - 0.0070 in/in
on Tensile Bar; SABIC Method
0.0050 - 0.0070 cm/cm

@Thickness 3.20 mm
0.0050 - 0.0070 in/in

@Thickness 0.126 in
SABIC Method
Linear Mold Shrinkage, Transverse 0.0050 - 0.0070 cm/cm

@Thickness 3.20 mm
0.0050 - 0.0070 in/in

@Thickness 0.126 in
SABIC Method
Melt Flow 12.5 g/10 min

@Load 6.60 kg,
Temperature 367 °C
12.5 g/10 min

@Load 14.6 lb,
Temperature 693 °F
ASTM D1238
Melt Index of Compound 8.0 g/10 min

@Load 5.00 kg,
Temperature 360 °C
8.0 g/10 min

@Load 11.0 lb,
Temperature 680 °F
MVR [cm^3/10 min]; ISO 1133
Mechanical Properties Metric English Comments
Hardness, H358/30 140 MPa
20300 psi
ISO 2039-1
Tensile Strength at Break 78.0 MPa
11300 psi
5 mm/min; ISO 527
96.0 MPa
13900 psi
Type I, 5 mm/min; ASTM D638
Tensile Strength, Yield 95.0 MPa
13800 psi
5 mm/min; ISO 527
96.0 MPa
13900 psi
Type I, 5 mm/min; ASTM D638
Elongation at Break 16.8 %
16.8 %
5 mm/min; ISO 527
25 %
25 %
Type I, 5 mm/min; ASTM D638
Elongation at Yield 6.0 %
6.0 %
Type I, 5 mm/min; ASTM D638
8.5 %
8.5 %
5 mm/min; ISO 527
Tensile Modulus 3.11 GPa
451 ksi
1 mm/min; ISO 527
3.51 GPa
509 ksi
5 mm/min; ASTM D638
Flexural Strength 159 MPa
23100 psi
1.3 mm/min, 50 mm span; ASTM D790
Flexural Yield Strength 123 MPa
17800 psi
2 mm/min; ISO 178
155 MPa
22500 psi
2.6 mm/min, 100 mm span; ASTM D790
Flexural Modulus 3.08 GPa
447 ksi
2 mm/min; ISO 178
3.10 GPa
450 ksi
2.6 mm/min, 100 mm span; ASTM D790
3.17 GPa
460 ksi
1.3 mm/min, 50 mm span; ASTM D790
Izod Impact, Notched 0.690 J/cm
1.29 ft-lb/in
ASTM D256
0.740 J/cm

@Temperature -30.0 °C
1.39 ft-lb/in

@Temperature -22.0 °F
ASTM D256
Izod Impact, Unnotched NB
NB
ASTM D4812
Izod Impact, Notched (ISO) 4.00 kJ/m²
1.90 ft-lb/in²
80*10*4; ISO 180/1A
5.00 kJ/m²

@Temperature -30.0 °C
2.38 ft-lb/in²

@Temperature -22.0 °F
80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) NB
NB
80*10*4; ISO 180/1U
NB

@Temperature -30.0 °C
NB

@Temperature -22.0 °F
80*10*4; ISO 180/1U
Charpy Impact Unnotched NB
NB
Edgew 80*10*4 sp=62mm; ISO 179/1eU
NB

@Temperature -30.0 °C
NB

@Temperature -22.0 °F
Edgew 80*10*4 sp=62mm; ISO 179/1eU
Dart Drop, Total Energy 33.0 J

@Temperature 23.0 °C
24.3 ft-lb

@Temperature 73.4 °F
ASTM D3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 50.0 µm/m-°C

@Temperature -40.0 - 150 °C
27.8 µin/in-°F

@Temperature -40.0 - 302 °F
ASTM E 831
50.0 µm/m-°C

@Temperature 23.0 - 150 °C
27.8 µin/in-°F

@Temperature 73.4 - 302 °F
ISO 11359-2
CTE, linear, Transverse to Flow 50.0 µm/m-°C

@Temperature -40.0 - 150 °C
27.8 µin/in-°F

@Temperature -40.0 - 302 °F
ASTM E 831
50.0 µm/m-°C

@Temperature 23.0 - 150 °C
27.8 µin/in-°F

@Temperature 73.4 - 302 °F
ISO 11359-2
Thermal Conductivity 0.220 W/m-K
1.53 BTU-in/hr-ft²-°F
ASTM E 1530
Deflection Temperature at 0.46 MPa (66 psi) 222 °C

@Thickness 3.20 mm
432 °F

@Thickness 0.126 in
unannealed; ASTM D648
237 °C

@Thickness 6.40 mm
459 °F

@Thickness 0.252 in
unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 228 °C
442 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
217 °C

@Thickness 3.20 mm
423 °F

@Thickness 0.126 in
unannealed; ASTM D648
230 °C

@Thickness 6.40 mm
446 °F

@Thickness 0.252 in
unannealed; ASTM D648
Vicat Softening Point 238 °C
460 °F
Rate B/120; ISO 306
242 °C
468 °F
Rate B/50; ASTM D1525
242 °C
468 °F
Rate B/50; ISO 306
Glass Transition Temp, Tg 247 °C
477 °F
Oxygen Index 45 %
45 %
ISO 4589
Glow Wire Test 850 °C
1560 °F
IEC 60695-2-13
960 °C

@Thickness 3.20 mm
1760 °F

@Thickness 0.126 in
IEC 60695-2-12
Optical Properties Metric English Comments
Haze 2.0 %

@Thickness 2.54 mm
2.0 %

@Thickness 0.100 in
ASTM D1003
Transmission, Visible 58 %
58 %
2.54 mm; ASTM D1003
Electrical Properties Metric English Comments
Dielectric Strength 17.0 kV/mm

@Thickness 3.20 mm
432 kV/in

@Thickness 0.126 in
in oil; ASTM D149
Dissipation Factor 0.0010

@Frequency 1000 Hz
0.0010

@Frequency 1000 Hz
IEC 60250
0.0070

@Frequency 1.00e+6 Hz
0.0070

@Frequency 1.00e+6 Hz
IEC 60250
0.0080

@Frequency 100 Hz
0.0080

@Frequency 100 Hz
IEC 60250
0.025

@Frequency 50.0 - 60.0 Hz
0.025

@Frequency 50.0 - 60.0 Hz
IEC 60250
Comparative Tracking Index 175 V
175 V
IEC 60112
Descriptive Properties Value Comments
Ball Pressure Test, 125°C +/- 2°C Passes
IEC 60695-10-2