SABIC Innovative Plastics ULTEM HU2100 PEI (Asia Pacific)
| Category | Polymer , Thermoplastic , Polyetherimide (PEI) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | ULTEM |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics ULTEM HU2100 PEI (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
10% Glass fiber filled, standard flow Polyetherimide (Tg 217C). US FDA and European Food Contact approved. For medical devices and pharmaceutical applications.Healthcare management of change, biocompatible (ISO 10993 or USP Class VI).
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.34 g/cc | 1.34 g/cc | ASTM D792 |
| Density | 1.34 g/cc | 0.0484 lb/in³ | ISO 1183 |
| Moisture Absorption | 0.600 % | 0.600 % | 23°C / 50% RH; ISO 62 |
| Water Absorption at Saturation | 1.0 % | 1.0 % | ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0060 cm/cm @Thickness 3.20 mm |
0.0050 - 0.0060 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Flow | 5.0 g/10 min @Load 3.80 kg, Temperature 200 °C |
5.0 g/10 min @Load 8.38 lb, Temperature 392 °F |
ASTM D1238 |
| Melt Index of Compound | 9.0 g/10 min @Load 5.00 kg, Temperature 360 °C |
9.0 g/10 min @Load 11.0 lb, Temperature 680 °F |
MVR [cm^3/10 min]; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 115 MPa | 16700 psi | Type I, 5 mm/min; ASTM D638 |
| 115 MPa | 16700 psi | 5 mm/min; ISO 527 | |
| Tensile Strength, Yield | 114 MPa | 16500 psi | Type I, 5 mm/min; ASTM D638 |
| 115 MPa | 16700 psi | 5 mm/min; ISO 527 | |
| Elongation at Break | 4.0 % | 4.0 % | 5 mm/min; ISO 527 |
| 6.0 % | 6.0 % | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Yield | 4.0 % | 4.0 % | 5 mm/min; ISO 527 |
| 6.0 % | 6.0 % | Type I, 5 mm/min; ASTM D638 | |
| Tensile Modulus | 4.50 GPa | 653 ksi | 1 mm/min; ISO 527 |
| 4.68 GPa | 679 ksi | 5 mm/min; ASTM D638 | |
| Flexural Strength | 185 MPa | 26800 psi | 2 mm/min; ISO 178 |
| Flexural Yield Strength | 160 MPa | 23200 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 4.50 GPa | 653 ksi | 2 mm/min; ISO 178 |
| 5.50 GPa | 798 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 0.530 J/cm | 0.993 ft-lb/in | ASTM D256 |
| 0.530 J/cm @Temperature -30.0 °C |
0.993 ft-lb/in @Temperature -22.0 °F |
ASTM D256 | |
| Izod Impact, Unnotched (ISO) | 30.0 kJ/m² | 14.3 ft-lb/in² | 80*10*4; ISO 180/1U |
| 30.0 kJ/m² @Temperature -30.0 °C |
14.3 ft-lb/in² @Temperature -22.0 °F |
80*10*4; ISO 180/1U | |
| Charpy Impact, Notched | 0.700 J/cm² | 3.33 ft-lb/in² | Edgew 80*10*4 sp=62mm; ISO 179/1eA |
| Dart Drop, Total Energy | 10.0 J @Temperature 23.0 °C |
7.38 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 26.0 µm/m-°C @Temperature 23.0 - 150 °C |
14.4 µin/in-°F @Temperature 73.4 - 302 °F |
ISO 11359-2 |
| 32.4 µm/m-°C @Temperature -40.0 - 40.0 °C |
18.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 | |
| CTE, linear, Transverse to Flow | 60.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
33.3 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 60.0 µm/m-°C @Temperature 23.0 - 150 °C |
33.3 µin/in-°F @Temperature 73.4 - 302 °F |
ISO 11359-2 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 205 °C | 401 °F | Edgew 120*10*4 sp=100mm; ISO 75/Ae |
| 205 °C @Thickness 3.20 mm |
401 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Vicat Softening Point | 212 °C | 414 °F | Rate B/50; ISO 306 |
| 217 °C | 423 °F | Rate B/120; ISO 306 | |
| 223 °C | 433 °F | Rate B/50; ASTM D1525 | |
| Glass Transition Temp, Tg | 217 °C | 423 °F | |
| UL RTI, Electrical | 170 °C | 338 °F | UL 746B |
| UL RTI, Mechanical with Impact | 170 °C | 338 °F | UL 746B |
| UL RTI, Mechanical without Impact | 170 °C | 338 °F | UL 746B |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dielectric Strength | 15.0 kV/mm @Thickness 3.20 mm |
381 kV/in @Thickness 0.126 in |
in oil; IEC 60243-1 |
| Comparative Tracking Index | 150 V | 150 V | IEC 60112 |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Lexan® XHT4143 PC Copolymer (Asia Pacific)
- Minelco Mulcoa 60
- Taiwan PU Corporation TPU-C95 General Grade, Calender Molding Polyester Base TPU
- Spartech Royalite R570 FR-ABS Fire Rated Sheet
- Plenco 00755 Melamine-Phenolic, Granular, Injection Molded
- EMS-Grivory Grivory® AG-30 H PA66
- Daikin NEOFLON ND-4 FEP Dispersion, Milky White
Copyright © lookpolymers.com All Rights Reserved