SABIC Innovative Plastics ULTEM HU1110 PEI (Asia Pacific)

Category Polymer , Thermoplastic , Polyetherimide (PEI)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name ULTEM
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics ULTEM HU1110 PEI (Asia Pacific).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Enhanced flow Polyetherimide (Tg 217C). ECO Conforming. For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible (ISO 10993 or USP Class VI), food contact compliant. EtO and steam sterilizable. NSF 51 listing, compliant in recognized colors.
Physical Properties Metric English Comments
Specific Gravity 1.36 g/cc
1.36 g/cc
ASTM D792
Density 1.27 g/cc
0.0459 lb/in³
ISO 1183
Moisture Absorption 0.650 %
0.650 %
23°C / 50% RH; ISO 62
Water Absorption at Saturation 1.2 %
1.2 %
ISO 62
Linear Mold Shrinkage, Flow 0.0050 - 0.0070 cm/cm

@Thickness 3.20 mm
0.0050 - 0.0070 in/in

@Thickness 0.126 in
SABIC Method
Melt Flow 16 g/10 min

@Load 6.60 kg,
Temperature 337 °C
16 g/10 min

@Load 14.6 lb,
Temperature 639 °F
ASTM D1238
Melt Index of Compound 21 g/10 min

@Load 5.00 kg,
Temperature 360 °C
21 g/10 min

@Load 11.0 lb,
Temperature 680 °F
MVR [cm^3/10 min]; ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break 80.0 MPa
11600 psi
5 mm/min; ISO 527
85.0 MPa
12300 psi
Type I, 5 mm/min; ASTM D638
Tensile Strength, Yield 110 MPa
16000 psi
Type I, 5 mm/min; ASTM D638
110 MPa
16000 psi
5 mm/min; ISO 527
Elongation at Break 60 %
60 %
5 mm/min; ISO 527
70 %
70 %
Type I, 5 mm/min; ASTM D638
Elongation at Yield 6.0 %
6.0 %
5 mm/min; ISO 527
7.0 %
7.0 %
Type I, 5 mm/min; ASTM D638
Tensile Modulus 3.50 GPa
508 ksi
1 mm/min; ISO 527
3.72 GPa
540 ksi
5 mm/min; ASTM D638
Flexural Yield Strength 140 MPa
20300 psi
2 mm/min; ISO 178
165 MPa
23900 psi
2.6 mm/min, 100 mm span; ASTM D790
174 MPa
25200 psi
1.3 mm/min, 50 mm span; ASTM D790
Flexural Modulus 3.30 GPa
479 ksi
2 mm/min; ISO 178
3.42 GPa
496 ksi
1.3 mm/min, 50 mm span; ASTM D790
3.72 GPa
540 ksi
2.6 mm/min, 100 mm span; ASTM D790
Izod Impact, Notched 0.560 J/cm
1.05 ft-lb/in
ASTM D256
Izod Impact, Notched (ISO) 4.00 kJ/m²
1.90 ft-lb/in²
80*10*4; ISO 180/1A
4.00 kJ/m²

@Temperature -30.0 °C
1.90 ft-lb/in²

@Temperature -22.0 °F
80*10*4; ISO 180/1A
Charpy Impact, Notched 0.500 J/cm²
2.38 ft-lb/in²
Edgew 80*10*4 sp=62mm; ISO 179/1eA
Gardner Impact 23.0 J
17.0 ft-lb
ASTM D3029
Dart Drop, Total Energy 28.0 J

@Temperature 23.0 °C
20.7 ft-lb

@Temperature 73.4 °F
ASTM D3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 55.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
30.6 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
55.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
30.6 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
CTE, linear, Transverse to Flow 55.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
30.6 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
55.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
30.6 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
Deflection Temperature at 1.8 MPa (264 psi) 210 °C
410 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
198 °C

@Thickness 6.40 mm
388 °F

@Thickness 0.252 in
unannealed; ASTM D648
Vicat Softening Point 200 °C
392 °F
Rate B/50; ISO 306
205 °C
401 °F
Rate B/120; ISO 306
219 °C
426 °F
Rate B/50; ASTM D1525
Glass Transition Temp, Tg 217 °C
423 °F
Flammability, UL94 V-2

@Thickness 0.710 mm
V-2

@Thickness 0.0280 in
UL 94
V-0

@Thickness 0.710 mm
V-0

@Thickness 0.0280 in
UL 94
5VA

@Thickness 3.00 mm
5VA

@Thickness 0.118 in
UL 94