SABIC Innovative Plastics ULTEM DU242 PEI
| Category | Polymer , Thermoplastic , Polyetherimide (PEI) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | ULTEM |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics ULTEM DU242 PEI.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Enhanced low temperature impact, high flow Polyetherimide blend. ECO Conforming.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.24 g/cc | 1.24 g/cc | ASTM D792 |
| Melt Flow | 30 g/10 min @Load 6.60 kg, Temperature 337 °C |
30 g/10 min @Load 14.6 lb, Temperature 639 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 74.0 MPa | 10700 psi | Type I, 5 mm/min; ASTM D638 |
| Elongation at Break | 67 % | 67 % | Type I, 5 mm/min; ASTM D638 |
| Tensile Modulus | 2.58 GPa | 374 ksi | 5 mm/min; ASTM D638 |
| Flexural Yield Strength | 112 MPa | 16200 psi | 2.6 mm/min, 100 mm span; ASTM D790 |
| Flexural Modulus | 2.51 GPa | 364 ksi | 2.6 mm/min, 100 mm span; ASTM D790 |
| Izod Impact, Notched | 1.81 J/cm | 3.39 ft-lb/in | ASTM D256 |
| 20.45 J/cm @Thickness 3.20 mm |
38.31 ft-lb/in @Thickness 0.126 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 160 °C @Thickness 6.40 mm |
320 °F @Thickness 0.252 in |
unannealed; ASTM D648 |