SABIC Innovative Plastics ULTEM CRS5211R PEI

Category Polymer , Thermoplastic , Polyetherimide (PEI)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name ULTEM
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics ULTEM CRS5211R PEI.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
20% Glass fiber filled, enhanced flow Polyetherimide copolymer (Tg 225C) with internal mold release and enhanced chemical resistance to strong acids, bases, aromatics, and ketones. ECO conforming.
Physical Properties Metric English Comments
Specific Gravity 1.45 g/cc
1.45 g/cc
ASTM D792
Melt Flow 5.5 g/10 min

@Load 6.60 kg,
Temperature 337 °C
5.5 g/10 min

@Load 14.6 lb,
Temperature 639 °F
ASTM D1238
Mechanical Properties Metric English Comments
Tensile Strength at Break 144 MPa
20900 psi
Type I, 5 mm/min; ASTM D638
Tensile Strength, Yield 137 MPa
19900 psi
Type I, 5 mm/min; ASTM D638
Elongation at Break 3.0 %
3.0 %
Type I, 5 mm/min; ASTM D638
Tensile Modulus 6.89 GPa
999 ksi
5 mm/min; ASTM D638
Flexural Yield Strength 213 MPa
30900 psi
2.6 mm/min, 100 mm span; ASTM D790
Flexural Modulus 6.89 GPa
999 ksi
2.6 mm/min, 100 mm span; ASTM D790
Izod Impact, Notched 0.740 J/cm
1.39 ft-lb/in
ASTM D256
4.59 J/cm

@Thickness 3.20 mm
8.60 ft-lb/in

@Thickness 0.126 in
ASTM D256
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 218 °C

@Thickness 6.40 mm
424 °F

@Thickness 0.252 in
unannealed; ASTM D648
Glass Transition Temp, Tg 225 °C
437 °F