SABIC Innovative Plastics ULTEM CRS5001 PEI

Category Polymer , Thermoplastic , Polyetherimide (PEI)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name ULTEM
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics ULTEM CRS5001 PEI.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Transparent, Standard flow Polyetherimide copolymer (Tg 225C) with enhanced chemical resistance to strong acids, bases, aromatics, and ketones. ECO conforming, UL94 V0 listing.
Physical Properties Metric English Comments
Specific Gravity 1.28 g/cc
1.28 g/cc
ASTM D792
Water Absorption 0.16 %

@Time 86400 sec
0.16 %

@Time 24.0 hour
ASTM D570
Linear Mold Shrinkage, Flow 0.0040 - 0.0070 cm/cm

@Thickness 3.20 mm
0.0040 - 0.0070 in/in

@Thickness 0.126 in
SABIC Method
Melt Flow 4.2 g/10 min

@Load 6.60 kg,
Temperature 337 °C
4.2 g/10 min

@Load 14.6 lb,
Temperature 639 °F
ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Rockwell R 123
123
ASTM D785
Tensile Strength, Yield 99.0 MPa
14400 psi
Type I, 5 mm/min; ASTM D638
Elongation at Break 60 %
60 %
Type I, 5 mm/min; ASTM D638
Tensile Modulus 2.89 GPa
419 ksi
5 mm/min; ASTM D638
Flexural Yield Strength 137 MPa
19900 psi
2.6 mm/min, 100 mm span; ASTM D790
Flexural Modulus 3.10 GPa
450 ksi
2.6 mm/min, 100 mm span; ASTM D790
Izod Impact, Notched 0.640 J/cm
1.20 ft-lb/in
ASTM D256
20.82 J/cm

@Thickness 3.20 mm
39.00 ft-lb/in

@Thickness 0.126 in
ASTM D256
Izod Impact, Unnotched 12.81 J/cm
24.00 ft-lb/in
ASTM D4812
Taber Abrasion, mg/1000 Cycles 10
10
CS-17, 1 kg; ASTM D1044
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 207 °C

@Thickness 6.40 mm
405 °F

@Thickness 0.252 in
unannealed; ASTM D648
Glass Transition Temp, Tg 225 °C
437 °F
UL RTI, Electrical 160 °C
320 °F
UL 746B
UL RTI, Mechanical with Impact 160 °C
320 °F
UL 746B
UL RTI, Mechanical without Impact 160 °C
320 °F
UL 746B
Flammability, UL94 V-0

@Thickness 1.49 mm
V-0

@Thickness 0.0587 in
UL 94
Optical Properties Metric English Comments
Transmission, Visible 90 %
90 %
transparent; thickness not quantified
Electrical Properties Metric English Comments
Volume Resistivity 1.10e+17 ohm-cm
1.10e+17 ohm-cm
ASTM D257
Surface Resistance 5.80e+16 ohm
5.80e+16 ohm
ASTM D257
Dielectric Constant 3.12

@Frequency 100 Hz
3.12

@Frequency 100 Hz
ASTM D150
Dielectric Strength 17.9 kV/mm

@Thickness 3.20 mm
455 kV/in

@Thickness 0.126 in
in oil; ASTM D149
Dissipation Factor 0.0017

@Frequency 100 Hz
0.0017

@Frequency 100 Hz
ASTM D150
Arc Resistance 120 - 180 sec
120 - 180 sec
Tungsten; ASTM D495
Comparative Tracking Index 100 - 175 V
100 - 175 V
UL 746A
Hot Wire Ignition, HWI >= 120 sec
>= 120 sec
UL 746A
High Amp Arc Ignition, HAI >= 120 arcs
>= 120 arcs
UL 746A
High Voltage Arc-Tracking Rate, HVTR 80.0 - 150 mm/min
3.15 - 5.91 in/min
UL 746A