SABIC Innovative Plastics ULTEM 9011 PEI (Asia Pacific)

Category Polymer , Thermoplastic , Polyetherimide (PEI)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name ULTEM
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics ULTEM 9011 PEI (Asia Pacific).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Transparent, high flow Polyetherimide (Tg 217C). ECO Conforming. Improved processability for Fiber extrusion.
Physical Properties Metric English Comments
Specific Gravity 1.27 g/cc
1.27 g/cc
ASTM D792
Density 1.27 g/cc
0.0459 lb/in³
ISO 1183
Moisture Absorption 0.700 %
0.700 %
23°C / 50% RH; ISO 62
Water Absorption at Saturation 1.25 %
1.25 %
ISO 62
Linear Mold Shrinkage, Flow 0.0050 - 0.0070 cm/cm
0.0050 - 0.0070 in/in
on Tensile Bar; SABIC Method
0.0050 - 0.0070 cm/cm

@Thickness 3.20 mm
 0.0050 - 0.0070 in/in

@Thickness 0.126 in
 SABIC Method
Linear Mold Shrinkage, Transverse 0.0050 - 0.0070 cm/cm

@Thickness 3.20 mm
 0.0050 - 0.0070 in/in

@Thickness 0.126 in
 SABIC Method
Melt Flow 17.8 g/10 min

@Load 6.60 kg,
Temperature 337 °C
 17.8 g/10 min

@Load 14.6 lb,
Temperature 639 °F
 ASTM D1238
Melt Index of Compound 25 g/10 min

@Load 5.00 kg,
Temperature 360 °C
 25 g/10 min

@Load 11.0 lb,
Temperature 680 °F
 MVR [cm^3/10 min]; ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break 85.0 MPa
12300 psi
5 mm/min; ISO 527
105 MPa
15200 psi
Type I, 5 mm/min; ASTM D638
Tensile Strength, Yield 105 MPa
15200 psi
5 mm/min; ISO 527
110 MPa
16000 psi
Type I, 5 mm/min; ASTM D638
Elongation at Break 60 %
60 %
Type I, 5 mm/min; ASTM D638
60 %
60 %
5 mm/min; ISO 527
Elongation at Yield 6.0 %
6.0 %
5 mm/min; ISO 527
7.0 %
7.0 %
Type I, 5 mm/min; ASTM D638
Tensile Modulus 3.20 GPa
464 ksi
1 mm/min; ISO 527
3.59 GPa
521 ksi
5 mm/min; ASTM D638
Flexural Yield Strength 160 MPa
23200 psi
2 mm/min; ISO 178
165 MPa
23900 psi
1.3 mm/min, 50 mm span; ASTM D790
Flexural Modulus 3.30 GPa
479 ksi
2 mm/min; ISO 178
3.52 GPa
511 ksi
1.3 mm/min, 50 mm span; ASTM D790
Izod Impact, Notched 0.320 J/cm
0.599 ft-lb/in
ASTM D256
0.350 J/cm

@Temperature -30.0 °C
 0.656 ft-lb/in

@Temperature -22.0 °F
 ASTM D256
11.75 J/cm

@Thickness 3.20 mm
 22.01 ft-lb/in

@Thickness 0.126 in
 ASTM D256
Izod Impact, Unnotched 13.35 J/cm
25.01 ft-lb/in
ASTM D4812
Izod Impact, Notched (ISO) 5.00 kJ/m²
2.38 ft-lb/in²
80*10*4; ISO 180/1A
5.00 kJ/m²

@Temperature -30.0 °C
 2.38 ft-lb/in²

@Temperature -22.0 °F
 80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) NB
NB
80*10*4; ISO 180/1U
NB

@Temperature -30.0 °C
 NB

@Temperature -22.0 °F
 80*10*4; ISO 180/1U
Charpy Impact, Notched 0.300 J/cm²
1.43 ft-lb/in²
Edgew 80*10*4 sp=62mm; ISO 179/1eA
Dart Drop, Total Energy 33.0 J

@Temperature 23.0 °C
 24.3 ft-lb

@Temperature 73.4 °F
 ASTM D3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 50.0 µm/m-°C

@Temperature 23.0 - 150 °C
 27.8 µin/in-°F

@Temperature 73.4 - 302 °F
 ISO 11359-2
55.0 µm/m-°C

@Temperature -40.0 - 150 °C
 30.6 µin/in-°F

@Temperature -40.0 - 302 °F
 ASTM E 831
CTE, linear, Transverse to Flow 50.0 µm/m-°C

@Temperature 23.0 - 150 °C
 27.8 µin/in-°F

@Temperature 73.4 - 302 °F
 ISO 11359-2
55.0 µm/m-°C

@Temperature -40.0 - 150 °C
 30.6 µin/in-°F

@Temperature -40.0 - 302 °F
 ASTM E 831
Deflection Temperature at 0.46 MPa (66 psi) 200 °C
392 °F
Edgew 120*10*4 sp=100mm; ISO 75/Be
205 °C

@Thickness 3.20 mm
 401 °F

@Thickness 0.126 in
 unannealed; ASTM D648
207 °C

@Thickness 6.40 mm
 405 °F

@Thickness 0.252 in
 unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 190 °C
374 °F
Edgew 120*10*4 sp=100mm; ISO 75/Ae
193 °C
379 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
197 °C

@Thickness 3.20 mm
 387 °F

@Thickness 0.126 in
 unannealed; ASTM D648
199 °C

@Thickness 6.40 mm
 390 °F

@Thickness 0.252 in
 unannealed; ASTM D648
Vicat Softening Point 211 °C
412 °F
Rate B/50; ISO 306
212 °C
414 °F
Rate B/120; ISO 306
215 °C
419 °F
Rate A/50; ISO 306
219 °C
426 °F
Rate B/50; ASTM D1525
Glass Transition Temp, Tg 217 °C
423 °F
Oxygen Index 44 %
44 %
ASTM D2863
Optical Properties Metric English Comments
Transmission, Visible 90 %
90 %
transparent; thickness not quantified
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+17 ohm-cm
1.00e+17 ohm-cm
ASTM D257
Dielectric Constant 3.15

@Frequency 1000 Hz
 3.15

@Frequency 1000 Hz
 ASTM D150
Dielectric Strength 28.0 kV/mm

@Thickness 1.60 mm
 711 kV/in

@Thickness 0.0630 in
 in oil; ASTM D149
32.7 kV/mm

@Thickness 1.60 mm
 831 kV/in

@Thickness 0.0630 in
 in air; ASTM D149
Dissipation Factor 0.0013

@Frequency 1000 Hz
 0.0013

@Frequency 1000 Hz
 ASTM D150
0.0025

@Frequency 2.45e+9 Hz
 0.0025

@Frequency 2.45e+9 Hz
 ASTM D150
Arc Resistance 120 - 180 sec
120 - 180 sec
Tungsten; ASTM D495
Comparative Tracking Index 100 - 175 V
100 - 175 V
UL 746A
Hot Wire Ignition, HWI 60 - 120 sec
60 - 120 sec
UL 746A
High Amp Arc Ignition, HAI 15 - 30 arcs
15 - 30 arcs
UL 746A
High Voltage Arc-Tracking Rate, HVTR 25.4 - 80.0 mm/min
1.00 - 3.15 in/min
UL 746A
Descriptive Properties Value Comments
Ball Pressure Test, 125°C +/- 2°C Passes
IEC 60695-10-2