SABIC Innovative Plastics ULTEM 4001 PEI
| Category | Polymer , Thermoplastic , Polyetherimide (PEI) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | ULTEM |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics ULTEM 4001 PEI.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
PTFE filled, standard flow Polyetherimide (Tg 217C). ECO Conforming, UL94 V0 and 5VA listing.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.33 g/cc | 1.33 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm |
0.0050 - 0.0070 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Flow | 9.5 g/10 min @Load 6.60 kg, Temperature 337 °C |
9.5 g/10 min @Load 14.6 lb, Temperature 639 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell M | 110 | 110 | ASTM D785 |
| Tensile Strength, Yield | 103 MPa | 14900 psi | Type I, 5 mm/min; ASTM D638 |
| Elongation at Break | 40 % | 40 % | Type I, 5 mm/min; ASTM D638 |
| Tensile Modulus | 3.35 GPa | 486 ksi | 5 mm/min; ASTM D638 |
| Flexural Yield Strength | 151 MPa | 21900 psi | 2.6 mm/min, 100 mm span; ASTM D790 |
| Flexural Modulus | 3.40 GPa | 493 ksi | 2.6 mm/min, 100 mm span; ASTM D790 |
| Izod Impact, Notched | 1.17 J/cm | 2.19 ft-lb/in | ASTM D256 |
| 12.81 J/cm @Thickness 3.20 mm |
24.00 ft-lb/in @Thickness 0.126 in |
ASTM D256 | |
| Izod Impact, Unnotched | 5.34 J/cm | 10.0 ft-lb/in | ASTM D4812 |
| Coefficient of Friction, Dynamic | 0.25 | 0.25 | steel; ASTM D1894 |
| K (wear) Factor | 54.4 x 10-8 mm³/N-M | 27.0 x 10-10 in³-min/ft-lb-hr | PV=2000 psi-fpm vs Self; SABIC Method |
| 145 x 10-8 mm³/N-M | 72.0 x 10-10 in³-min/ft-lb-hr | PV=2000 psi-fpm vs Self; SABIC Method | |
| Limiting Pressure Velocity | 1.90 MPa-m/sec | 54200 psi-ft/min | 0.51 m/s; SABIC Method |
| Taber Abrasion, mg/1000 Cycles | 2.0 | 2.0 | CS-17, 1 kg; ASTM D1044 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 200 °C @Thickness 6.40 mm |
392 °F @Thickness 0.252 in |
unannealed; ASTM D648 |
| Glass Transition Temp, Tg | 217 °C | 423 °F | |
| UL RTI, Electrical | 170 °C | 338 °F | UL 746B |
| UL RTI, Mechanical with Impact | 170 °C | 338 °F | UL 746B |
| UL RTI, Mechanical without Impact | 170 °C | 338 °F | UL 746B |
| Flammability, UL94 | V-0 @Thickness 0.380 mm |
V-0 @Thickness 0.0150 in |
UL 94 |
| 5VA @Thickness 1.49 mm |
5VA @Thickness 0.0587 in |
UL 94 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Arc Resistance | 60 - 120 sec | 60 - 120 sec | Tungsten; ASTM D495 |
| Comparative Tracking Index | 100 - 175 V | 100 - 175 V | UL 746A |
| Hot Wire Ignition, HWI | 60 - 120 sec | 60 - 120 sec | UL 746A |
| High Amp Arc Ignition, HAI | >= 120 arcs | >= 120 arcs | UL 746A |
| High Voltage Arc-Tracking Rate, HVTR | 25.4 - 80.0 mm/min | 1.00 - 3.15 in/min | UL 746A |
Users viewing this material also viewed the following:
- PolyOne Synplast™ TOTM-E Tri (2-ethylhexyl) Trimellitate
- SABIC Innovative Plastics Cycoloy® MC8100 PC+ABS (Asia Pacific)
- Mitsubishi Xantar® F 25 UR Polycarbonate
- Schott N-SK16 Glass
- Shin-Etsu Silicones LIMSâ„¢ KE2095-40AB Elastomer
- A. Schulman PP 1500X-01 Polypropylene High Impact Copolymer Polypropylene
- Formosa Plastics Formolene® 3302B Random Copolymer Polypropylene
- Goodfellow Carbon/Vinyl Ester Tube
- Asahi Glass ASAHIKLIN AK-225ATE Hydrochlorofluorocarbon Solvent
- 3M FM041909 White Polyester Label Products
Copyright © lookpolymers.com All Rights Reserved