SABIC Innovative Plastics ULTEM 2410EPR PEI (Europe-Africa-Middle East)
| Category | Polymer , Thermoplastic , Polyetherimide (PEI) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | ULTEM |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics ULTEM 2410EPR PEI (Europe-Africa-Middle East).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
40% Glass fiber filled, high flow Polyetherimide (Tg 217C) with internal mold release for enhanced electroplatability. Resin is RoHS compliant. UL94 V0 listing.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.56 g/cc | 1.56 g/cc | ASTM D792 |
| Density | 1.56 g/cc | 0.0564 lb/in³ | ISO 1183 |
| Moisture Absorption | 0.400 % | 0.400 % | 23°C / 50% RH; ISO 62 |
| Water Absorption at Saturation | 0.80 % | 0.80 % | ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0020 - 0.0040 cm/cm | 0.0020 - 0.0040 in/in | on Tensile Bar; SABIC Method |
| 0.0020 - 0.0040 cm/cm @Thickness 3.20 mm |
0.0020 - 0.0040 in/in @Thickness 0.126 in |
SABIC Method | |
| Linear Mold Shrinkage, Transverse | 0.0030 - 0.0050 cm/cm @Thickness 3.20 mm |
0.0030 - 0.0050 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Flow | 8.9 g/10 min @Load 6.60 kg, Temperature 337 °C |
8.9 g/10 min @Load 14.6 lb, Temperature 639 °F |
ASTM D1238 |
| Melt Index of Compound | 11 g/10 min @Load 5.00 kg, Temperature 360 °C |
11 g/10 min @Load 11.0 lb, Temperature 680 °F |
MVR [cm^3/10 min]; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, H358/30 | 165 MPa | 23900 psi | ISO 2039-1 |
| Tensile Strength at Break | 165 MPa | 23900 psi | Type I, 5 mm/min; ASTM D638 |
| 170 MPa | 24700 psi | 5 mm/min; ISO 527 | |
| Tensile Strength, Yield | 165 MPa | 23900 psi | Type I, 5 mm/min; ASTM D638 |
| 170 MPa | 24700 psi | 5 mm/min; ISO 527 | |
| Elongation at Break | 1.8 % | 1.8 % | Type I, 5 mm/min; ASTM D638 |
| 2.0 % | 2.0 % | 5 mm/min; ISO 527 | |
| Elongation at Yield | 1.8 % | 1.8 % | Type I, 5 mm/min; ASTM D638 |
| 2.0 % | 2.0 % | 5 mm/min; ISO 527 | |
| Tensile Modulus | 11.0 GPa | 1600 ksi | 1 mm/min; ISO 527 |
| 11.1 GPa | 1610 ksi | 5 mm/min; ASTM D638 | |
| Flexural Yield Strength | 220 MPa | 31900 psi | 2 mm/min; ISO 178 |
| 240 MPa | 34800 psi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Flexural Modulus | 9.50 GPa | 1380 ksi | 2 mm/min; ISO 178 |
| 10.65 GPa | 1545 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 0.820 J/cm | 1.54 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 4.10 J/cm | 7.68 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 10.0 kJ/m² | 4.76 ft-lb/in² | 80*10*4; ISO 180/1A |
| 10.0 kJ/m² @Temperature -30.0 °C |
4.76 ft-lb/in² @Temperature -22.0 °F |
80*10*4; ISO 180/1A | |
| Izod Impact, Unnotched (ISO) | 30.0 kJ/m² | 14.3 ft-lb/in² | 80*10*4; ISO 180/1U |
| 30.0 kJ/m² @Temperature -30.0 °C |
14.3 ft-lb/in² @Temperature -22.0 °F |
80*10*4; ISO 180/1U | |
| Charpy Impact Unnotched | 3.00 J/cm² | 14.3 ft-lb/in² | Edgew 80*10*4 sp=62mm; ISO 179/1eU |
| 3.50 J/cm² @Temperature -30.0 °C |
16.7 ft-lb/in² @Temperature -22.0 °F |
Edgew 80*10*4 sp=62mm; ISO 179/1eU | |
| Charpy Impact, Notched | 1.00 J/cm² | 4.76 ft-lb/in² | Edgew 80*10*4 sp=62mm; ISO 179/1eA |
| 1.00 J/cm² @Temperature -30.0 °C |
4.76 ft-lb/in² @Temperature -22.0 °F |
Edgew 80*10*4 sp=62mm; ISO 179/1eA | |
| Dart Drop, Total Energy | 18.0 J @Temperature 23.0 °C |
13.3 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 15.0 µm/m-°C @Temperature -40.0 - 150 °C |
8.33 µin/in-°F @Temperature -40.0 - 302 °F |
ASTM E 831 |
| 15.0 µm/m-°C @Temperature 23.0 - 150 °C |
8.33 µin/in-°F @Temperature 73.4 - 302 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 45.0 µm/m-°C @Temperature -40.0 - 150 °C |
25.0 µin/in-°F @Temperature -40.0 - 302 °F |
ASTM E 831 |
| 45.0 µm/m-°C @Temperature 23.0 - 150 °C |
25.0 µin/in-°F @Temperature 73.4 - 302 °F |
ISO 11359-2 | |
| Thermal Conductivity | 0.300 W/m-K | 2.08 BTU-in/hr-ft²-°F | ISO 8302 |
| Deflection Temperature at 0.46 MPa (66 psi) | 206 °C | 403 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 208 °C | 406 °F | Edgew 120*10*4 sp=100mm; ISO 75/Be | |
| 212 °C @Thickness 3.20 mm |
414 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| 215 °C @Thickness 6.40 mm |
419 °F @Thickness 0.252 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 197 °C | 387 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 205 °C | 401 °F | Edgew 120*10*4 sp=100mm; ISO 75/Ae | |
| 204 °C @Thickness 3.20 mm |
399 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| 208 °C @Thickness 6.40 mm |
406 °F @Thickness 0.252 in |
unannealed; ASTM D648 | |
| Vicat Softening Point | 214 °C | 417 °F | Rate B/50; ISO 306 |
| 215 °C | 419 °F | Rate B/120; ISO 306 | |
| 223 °C | 433 °F | Rate B/50; ASTM D1525 | |
| Glass Transition Temp, Tg | 217 °C | 423 °F | |
| Flammability, UL94 | V-0 @Thickness 0.400 mm |
V-0 @Thickness 0.0157 in |
UL 94 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Arc Resistance | 120 - 180 sec | 120 - 180 sec | Tungsten; ASTM D495 |
| Comparative Tracking Index | 100 - 175 V | 100 - 175 V | UL 746A |
| Hot Wire Ignition, HWI | 7.0 - 15 sec | 7.0 - 15 sec | UL 746A |
| High Amp Arc Ignition, HAI | 0.00 - 15 arcs | 0.00 - 15 arcs | UL 746A |
| High Voltage Arc-Tracking Rate, HVTR | >= 150 mm/min | >= 5.91 in/min | UL 746A |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Ball Pressure Test, 125°C +/- 2°C | Passes | IEC 60695-10-2 |