SABIC Innovative Plastics ULTEM 2210F PEI
| Category | Polymer , Thermoplastic , Polyetherimide (PEI) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | ULTEM |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics ULTEM 2210F PEI.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
20% Glass fiber filled, enhanced flow Polyetherimide (Tg 217C). ECO Conforming. US FDA Food Contact compliant in recognized colors.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.42 g/cc | 0.0513 lb/in³ | ISO 1183 |
| Moisture Absorption | 0.550 % | 0.550 % | 23°C / 50% RH; ISO 62 |
| Water Absorption at Saturation | 1.0 % | 1.0 % | ISO 62 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 140 MPa | 20300 psi | Type I, 5 mm/min; ASTM D638 |
| 140 MPa | 20300 psi | 5 mm/min; ISO 527 | |
| Tensile Strength, Yield | 139 MPa | 20200 psi | Type I, 5 mm/min; ASTM D638 |
| 140 MPa | 20300 psi | 5 mm/min; ISO 527 | |
| Elongation at Break | 5.0 % | 5.0 % | 5 mm/min; ISO 527 |
| Elongation at Yield | 4.0 % | 4.0 % | Type I, 5 mm/min; ASTM D638 |
| 5.0 % | 5.0 % | 5 mm/min; ISO 527 | |
| Tensile Modulus | 6.80 GPa | 986 ksi | 1 mm/min; ISO 527 |
| 6.89 GPa | 999 ksi | 5 mm/min; ASTM D638 | |
| Flexural Yield Strength | 210 MPa | 30500 psi | 2 mm/min; ISO 178 |
| 227 MPa | 32900 psi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Flexural Modulus | 6.50 GPa | 943 ksi | 2 mm/min; ISO 178 |
| 6.89 GPa | 999 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Unnotched | 4.75 J/cm | 8.90 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 5.00 kJ/m² | 2.38 ft-lb/in² | 80*10*4; ISO 180/1A |
| 5.00 kJ/m² @Temperature -30.0 °C |
2.38 ft-lb/in² @Temperature -22.0 °F |
80*10*4; ISO 180/1A | |
| Charpy Impact, Notched | 0.800 J/cm² | 3.81 ft-lb/in² | Edgew 80*10*4 sp=62mm; ISO 179/1eA |
| Dart Drop, Total Energy | 13.0 J @Temperature 23.0 °C |
9.59 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 211 °C @Thickness 6.40 mm |
412 °F @Thickness 0.252 in |
unannealed; ASTM D648 |
| Vicat Softening Point | 212 °C | 414 °F | Rate B/50; ISO 306 |
| 218 °C | 424 °F | Rate B/120; ISO 306 | |
| 226 °C | 439 °F | Rate B/50; ASTM D1525 | |
| Glass Transition Temp, Tg | 217 °C | 423 °F |
Users viewing this material also viewed the following:
- Oxford Polymers Oxnilon 6-50GF 50% Glass Fiber Filled Nylon 6 for Injection Molding
- PolyOne Geon™ L4605 Red 7640 Polyvinyl Chloride, Semi-Rigid (PVC, Semi-Rigid)
- LyondellBasell Montell 0300 Polybutene
- LATI Laramid G/45 PPA, 45% Glass Fiber Reinforced
- Solvay TECHNYL® B 738 MX15 Grey 3279 PA66/6, 15% mineral filled
- SABIC Innovative Plastics LNP VERTON MV008SU PP
- SABIC Innovative Plastics LNP VERTON MV00AS PP (Europe-Africa-Middle East)
- Arlon 51583R020 0.020" (0.508 mm) Cured Silicone Rubber with Fiberglass Substrate
Copyright © lookpolymers.com All Rights Reserved