SABIC Innovative Plastics ULTEM 1100V PEI

Category Polymer , Thermoplastic , Polyetherimide (PEI)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name ULTEM
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics ULTEM 1100V PEI.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Transparent, standard flow Polyetherimide (Tg 217C). ECO Conforming, UL94 VO and 5VA listing; color dependant, see UL Yellow Card.
Physical Properties Metric English Comments
Specific Gravity 1.36 g/cc
1.36 g/cc
ASTM D792
Density 1.27 g/cc
0.0459 lb/in³
ISO 1183
Moisture Absorption 0.700 %
0.700 %
23°C / 50% RH; ISO 62
Water Absorption at Saturation 1.25 %
1.25 %
ISO 62
Linear Mold Shrinkage, Flow 0.0050 - 0.0070 cm/cm

@Thickness 3.20 mm
0.0050 - 0.0070 in/in

@Thickness 0.126 in
SABIC Method
Melt Flow 8.8 g/10 min

@Load 6.60 kg,
Temperature 337 °C
8.8 g/10 min

@Load 14.6 lb,
Temperature 639 °F
ASTM D1238
Melt Index of Compound 16 g/10 min

@Load 5.00 kg,
Temperature 220 °C
16 g/10 min

@Load 11.0 lb,
Temperature 428 °F
MVR [cm^3/10 min]; ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break 85.0 MPa
12300 psi
Type I, 5 mm/min; ASTM D638
85.0 MPa
12300 psi
5 mm/min; ISO 527
Tensile Strength, Yield 105 MPa
15200 psi
5 mm/min; ISO 527
110 MPa
16000 psi
Type I, 5 mm/min; ASTM D638
Elongation at Break 60 %
60 %
5 mm/min; ISO 527
70 %
70 %
Type I, 5 mm/min; ASTM D638
Elongation at Yield 6.0 %
6.0 %
5 mm/min; ISO 527
7.0 %
7.0 %
Type I, 5 mm/min; ASTM D638
Tensile Modulus 3.20 GPa
464 ksi
1 mm/min; ISO 527
3.72 GPa
540 ksi
5 mm/min; ASTM D638
Flexural Yield Strength 160 MPa
23200 psi
2 mm/min; ISO 178
173 MPa
25100 psi
1.3 mm/min, 50 mm span; ASTM D790
Flexural Modulus 3.30 GPa
479 ksi
2 mm/min; ISO 178
3.43 GPa
497 ksi
1.3 mm/min, 50 mm span; ASTM D790
Izod Impact, Notched 0.370 J/cm
0.693 ft-lb/in
ASTM D256
Izod Impact, Notched (ISO) 6.00 kJ/m²
2.86 ft-lb/in²
80*10*4; ISO 180/1A
6.00 kJ/m²

@Temperature -30.0 °C
2.86 ft-lb/in²

@Temperature -22.0 °F
80*10*4; ISO 180/1A
Charpy Impact, Notched 0.400 J/cm²
1.90 ft-lb/in²
Edgew 80*10*4 sp=62mm; ISO 179/1eA
Dart Drop, Total Energy 38.0 J

@Temperature 23.0 °C
28.0 ft-lb

@Temperature 73.4 °F
ASTM D3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 55.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
30.6 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
55.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
30.6 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
CTE, linear, Transverse to Flow 55.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
30.6 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
55.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
30.6 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
Deflection Temperature at 1.8 MPa (264 psi) 188 °C
370 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
198 °C

@Thickness 6.40 mm
388 °F

@Thickness 0.252 in
unannealed; ASTM D648
Vicat Softening Point 211 °C
412 °F
Rate B/50; ASTM D1525
211 °C
412 °F
Rate B/50; ISO 306
212 °C
414 °F
Rate B/120; ISO 306
Glass Transition Temp, Tg 217 °C
423 °F
Flammability, UL94 V-2

@Thickness 0.400 mm
V-2

@Thickness 0.0157 in
UL 94
V-1

@Thickness 0.750 mm
V-1

@Thickness 0.0295 in
UL 94
V-0

@Thickness 0.750 mm
V-0

@Thickness 0.0295 in
UL 94
5VA

@Thickness 3.00 mm
5VA

@Thickness 0.118 in
UL 94
Optical Properties Metric English Comments
Transmission, Visible 90 %
90 %
transparent; thickness not quantified
Electrical Properties Metric English Comments
Arc Resistance 120 - 180 sec
120 - 180 sec
Tungsten; ASTM D495
Comparative Tracking Index 100 - 175 V
100 - 175 V
UL 746A
Hot Wire Ignition, HWI 60 - 120 sec
60 - 120 sec
UL 746A
High Amp Arc Ignition, HAI 15 - 30 arcs
15 - 30 arcs
UL 746A
High Voltage Arc-Tracking Rate, HVTR 25.4 - 80.0 mm/min
1.00 - 3.15 in/min
UL 746A