SABIC Innovative Plastics ULTEM 1010 PEI

Category Polymer , Thermoplastic , Polyetherimide (PEI)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name ULTEM
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics ULTEM 1010 PEI.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Transparent, enhanced flow Polyetherimide (Tg 217C). ECO Conforming, UL94 V0 and 5VA listing. US FDA and EU Food Contact compliant, NSF 51 listing. Effective June 2007, this grade will no longer be supported with biocompatibility information and should not be used for medical applications which require biocompatibility. Alternative grade HU1010.
Physical Properties Metric English Comments
Specific Gravity 1.27 g/cc
1.27 g/cc
ASTM D792
Water Absorption 0.25 %

@Time 86400 sec
0.25 %

@Time 24.0 hour
ASTM D570
Moisture Absorption at Equilibrium 1.25 %
1.25 %
ASTM D570
Linear Mold Shrinkage, Flow 0.0050 - 0.0070 cm/cm

@Thickness 3.20 mm
0.0050 - 0.0070 in/in

@Thickness 0.126 in
SABIC Method
Melt Flow 17.8 g/10 min

@Load 6.60 kg,
Temperature 337 °C
17.8 g/10 min

@Load 14.6 lb,
Temperature 639 °F
ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Rockwell M 109
109
ASTM D785
Tensile Strength, Yield 110 MPa
16000 psi
Type I, 5 mm/min; ASTM D638
Elongation at Break 60 %
60 %
Type I, 5 mm/min; ASTM D638
Elongation at Yield 7.0 %
7.0 %
Type I, 5 mm/min; ASTM D638
Tensile Modulus 3.58 GPa
519 ksi
5 mm/min; ASTM D638
Flexural Yield Strength 165 MPa
23900 psi
2.6 mm/min, 100 mm span; ASTM D790
Flexural Modulus 3.51 GPa
509 ksi
2.6 mm/min, 100 mm span; ASTM D790
Izod Impact, Notched 0.320 J/cm
0.599 ft-lb/in
ASTM D256
11.74 J/cm

@Thickness 3.20 mm
21.99 ft-lb/in

@Thickness 0.126 in
ASTM D256
Izod Impact, Unnotched 13.35 J/cm
25.01 ft-lb/in
ASTM D4812
Gardner Impact 33.0 J
24.3 ft-lb
ASTM D3029
Taber Abrasion, mg/1000 Cycles 10
10
CS-17, 1 kg; ASTM D1044
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 55.8 µm/m-°C

@Temperature -20.0 - 150 °C
31.0 µin/in-°F

@Temperature -4.00 - 302 °F
ASTM E 831
Thermal Conductivity 0.220 W/m-K
1.53 BTU-in/hr-ft²-°F
ASTM C177
Deflection Temperature at 0.46 MPa (66 psi) 207 °C

@Thickness 6.40 mm
405 °F

@Thickness 0.252 in
unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 198 °C

@Thickness 6.40 mm
388 °F

@Thickness 0.252 in
unannealed; ASTM D648
Vicat Softening Point 218 °C
424 °F
Rate B/50; ASTM D1525
Glass Transition Temp, Tg 217 °C
423 °F
UL RTI, Electrical 170 °C
338 °F
UL 746B
UL RTI, Mechanical with Impact 170 °C
338 °F
UL 746B
UL RTI, Mechanical without Impact 170 °C
338 °F
UL 746B
Flammability, UL94 V-0

@Thickness 0.750 mm
V-0

@Thickness 0.0295 in
UL 94
5VA

@Thickness 3.00 mm
5VA

@Thickness 0.118 in
UL 94
Oxygen Index 44 %
44 %
ASTM D2863
Optical Properties Metric English Comments
Transmission, Visible 90 %
90 %
transparent; thickness not quantified
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+17 ohm-cm
1.00e+17 ohm-cm
ASTM D257
Dielectric Constant 3.15

@Frequency 1000 Hz
3.15

@Frequency 1000 Hz
ASTM D150
Dielectric Strength 27.9 kV/mm

@Thickness 1.60 mm
709 kV/in

@Thickness 0.0630 in
in oil; ASTM D149
32.6 kV/mm

@Thickness 1.60 mm
828 kV/in

@Thickness 0.0630 in
in air; ASTM D149
Dissipation Factor 0.0013

@Frequency 1000 Hz
0.0013

@Frequency 1000 Hz
ASTM D150
0.0025

@Frequency 2.45e+9 Hz
0.0025

@Frequency 2.45e+9 Hz
ASTM D150
Arc Resistance 120 - 180 sec
120 - 180 sec
Tungsten; ASTM D495
Comparative Tracking Index 100 - 175 V
100 - 175 V
UL 746A
Hot Wire Ignition, HWI 60 - 120 sec
60 - 120 sec
UL 746A
High Amp Arc Ignition, HAI 15 - 30 arcs
15 - 30 arcs
UL 746A
High Voltage Arc-Tracking Rate, HVTR 25.4 - 80.0 mm/min
1.00 - 3.15 in/min
UL 746A
Descriptive Properties Value Comments
NBS Smoke Density, Flaming, Ds 4 min 2
ASTM E 662