SABIC Innovative Plastics SABIC PPCOMPOUND 9710 PP

Category Polymer , Thermoplastic , Polypropylene (PP)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name SABIC PPCOMPOUND
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics SABIC PPCOMPOUND 9710 PP.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
SABIC® PPcompound 9710 is a mineral filled, impact modified polypropylene TPO. This material combines high impact resistance, scratch resistance, and heat stability with interior automotive UV stability. This material can exhibit ductility at temperatures as low as 0 degrees C. The IMDS is 164207488.
Physical Properties Metric English Comments
Specific Gravity 1.04 g/cc
1.04 g/cc
ASTM D792
Density 1.04 g/cc
0.0376 lb/in³
ISO 1183
Linear Mold Shrinkage, Flow 0.0050 cm/cm
0.0050 in/in
48 hrs @ 23°C, flow; SABIC Method
Linear Mold Shrinkage, Transverse 0.0090 cm/cm
0.0090 in/in
48 hrs @ 23°C, xflow; SABIC Method
Melt Flow 20 g/10 min

@Load 2.16 kg,
Temperature 230 °C
 20 g/10 min

@Load 4.76 lb,
Temperature 446 °F
 ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break 14.0 MPa
2030 psi
50 mm/min, 1A; ISO 527
Tensile Strength, Yield 20.0 MPa
2900 psi
50 mm/min; ISO 527
Elongation at Break 23.2 %
23.2 %
50 mm/min; ISO 527
Elongation at Yield 3.5 %
3.5 %
50 mm/min; ISO 527
Tensile Modulus 1.92 GPa
278 ksi
1 mm/min; ISO 527
Flexural Modulus 2.02 GPa
293 ksi
2 mm/min, 64mm span; ISO 178
Izod Impact, Notched (ISO) 18.0 kJ/m²
8.57 ft-lb/in²
80*10*4mm, Cut; ISO 180/1A
4.00 kJ/m²

@Temperature -30.0 °C
 1.90 ft-lb/in²

@Temperature -22.0 °F
 80*10*4mm, Cut; ISO 180/1A
6.00 kJ/m²

@Temperature 0.000 °C
 2.86 ft-lb/in²

@Temperature 32.0 °F
 80*10*4mm, Cut; ISO 180/1A
Charpy Impact, Notched 1.80 J/cm²
8.57 ft-lb/in²
80*10*4mm, Cut; ISO 179/1eA
0.300 J/cm²

@Temperature -30.0 °C
 1.43 ft-lb/in²

@Temperature -22.0 °F
 80*10*4mm, Cut; ISO 179/1eA
0.500 J/cm²

@Temperature 0.000 °C
 2.38 ft-lb/in²

@Temperature 32.0 °F
 80*10*4mm, Cut; ISO 179/1eA
Dart Drop, Total Energy 18.0 J

@Temperature 0.000 °C
 13.3 ft-lb

@Temperature 32.0 °F
 Instrumented Impact Energy @ peak, @ 6.6 m/s; ASTM D3763
19.0 J

@Temperature -30.0 °C
 14.0 ft-lb

@Temperature -22.0 °F
 Instrumented Impact Energy @ peak, -30°C @ 6.6 m/s; ASTM D3763
19.0 J

@Temperature 23.0 °C
 14.0 ft-lb

@Temperature 73.4 °F
 Instrumented Impact Energy @ peak, 6.6 m/s; ASTM D3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 49.0 µm/m-°C

@Temperature -30.0 - 100 °C
 27.2 µin/in-°F

@Temperature -22.0 - 212 °F
 ISO 11359-2
CTE, linear, Transverse to Flow 147 µm/m-°C

@Temperature -30.0 - 100 °C
 81.7 µin/in-°F

@Temperature -22.0 - 212 °F
 ISO 11359-2
Deflection Temperature at 0.46 MPa (66 psi) 109 °C
228 °F
80*10*4mm, Cut; ISO 75-1&2
Deflection Temperature at 1.8 MPa (264 psi) 59.0 °C
138 °F
80*10*4mm, Cut; ISO 75-1&2
Vicat Softening Point 133 °C
271 °F
10N, 50°C/hr; ISO 306