SABIC Innovative Plastics SABIC PPCOMPOUND 5310 PP
| Category | Polymer , Thermoplastic , Polypropylene (PP) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | SABIC PPCOMPOUND |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics SABIC PPCOMPOUND 5310 PP.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
SABIC® PPcompound 5310 is a mineral filled, impact modified polypropylene TPO. This material combines scratch resistance and heat stability with exterior automotive weathering stability. The IMDS ID is 209727767.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.960 g/cc | 0.960 g/cc | ASTM D792 |
| Density | 0.960 g/cc | 0.0347 lb/in³ | ISO 1183 |
| Melt Flow | 19 g/10 min @Load 2.16 kg, Temperature 230 °C |
19 g/10 min @Load 4.76 lb, Temperature 446 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 14.0 MPa | 2030 psi | 50 mm/min, 1A; ISO 527 |
| Tensile Strength, Yield | 21.0 MPa | 3050 psi | 50 mm/min; ISO 527 |
| Elongation at Break | 59.7 % | 59.7 % | 50 mm/min; ISO 527 |
| Elongation at Yield | 5.4 % | 5.4 % | 50 mm/min; ISO 527 |
| Tensile Modulus | 1.31 GPa | 190 ksi | 1 mm/min; ISO 527 |
| Flexural Modulus | 1.31 GPa | 190 ksi | 2 mm/min, 64mm span; ISO 178 |
| Izod Impact, Notched (ISO) | 26.0 kJ/m² | 12.4 ft-lb/in² | 80*10*4mm, Cut; ISO 180/1A |
| 3.00 kJ/m² @Temperature -30.0 °C |
1.43 ft-lb/in² @Temperature -22.0 °F |
80*10*4mm, Cut; ISO 180/1A | |
| Charpy Impact, Notched | 1.70 J/cm² | 8.09 ft-lb/in² | 80*10*4mm, Cut; ISO 179/1eA |
| 0.300 J/cm² @Temperature -30.0 °C |
1.43 ft-lb/in² @Temperature -22.0 °F |
80*10*4mm, Cut; ISO 179/1eA | |
| Dart Drop, Total Energy | 17.0 J @Temperature 23.0 °C |
12.5 ft-lb @Temperature 73.4 °F |
Instrumented Impact Energy @ peak, 6.6 m/s; ASTM D3763 |
| 23.0 J @Temperature -30.0 °C |
17.0 ft-lb @Temperature -22.0 °F |
Instrumented Impact Energy @ peak, -30°C @ 2.2 m/s; ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 99.0 µm/m-°C @Temperature -30.0 - 100 °C |
55.0 µin/in-°F @Temperature -22.0 - 212 °F |
ISO 11359-2 |
| CTE, linear, Transverse to Flow | 162 µm/m-°C @Temperature -30.0 - 100 °C |
90.0 µin/in-°F @Temperature -22.0 - 212 °F |
ISO 11359-2 |
| Deflection Temperature at 0.46 MPa (66 psi) | 92.0 °C | 198 °F | 80*10*4mm, Cut; ISO 75-1&2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 55.0 °C | 131 °F | 80*10*4mm, Cut; ISO 75-1&2 |
| Vicat Softening Point | 133 °C | 271 °F | 10N, 50°C/hr; ISO 306 |