SABIC Innovative Plastics SABIC PPCOMPOUND 19T1030 PP
| Category | Polymer , Thermoplastic , Polypropylene (PP) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | SABIC PPCOMPOUND |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics SABIC PPCOMPOUND 19T1030 PP.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
SABIC® PPcompound 19T1030 is a general purpose, talc filled, heat stabilized homopolymer polypropylene compound. This compound exhibits high flow and is suitable for injection molding applications. The IMDS ID is 278628419.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.16 g/cc | 1.16 g/cc | ASTM D792 |
| Density | 1.16 g/cc | 0.0419 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.0075 cm/cm | 0.0075 in/in | 48 hrs @ 23°C, flow; SABIC Method |
| Linear Mold Shrinkage, Transverse | 0.0125 cm/cm | 0.0125 in/in | 48 hrs @ 23°C, xflow; SABIC Method |
| Melt Flow | 16 g/10 min @Load 2.16 kg, Temperature 230 °C |
16 g/10 min @Load 4.76 lb, Temperature 446 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 33.0 MPa | 4790 psi | 50 mm/min, 1A; ISO 527 |
| Tensile Strength, Yield | 34.0 MPa | 4930 psi | 50 mm/min; ISO 527 |
| Elongation at Break | 4.0 % | 4.0 % | 50 mm/min; ISO 527 |
| Elongation at Yield | 3.0 % | 3.0 % | 50 mm/min; ISO 527 |
| Tensile Modulus | 4.75 GPa | 689 ksi | 1 mm/min; ISO 527 |
| Flexural Modulus | 4.10 GPa | 595 ksi | 2 mm/min, 64mm span; ISO 178 |
| Izod Impact, Notched (ISO) | 1.00 kJ/m² | 0.476 ft-lb/in² | 80*10*4mm, Cut; ISO 180/1A |
| 1.00 kJ/m² @Temperature -30.0 °C |
0.476 ft-lb/in² @Temperature -22.0 °F |
80*10*4mm, Cut; ISO 180/1A | |
| Charpy Impact, Notched | 0.100 J/cm² | 0.476 ft-lb/in² | 80*10*4mm, Cut; ISO 179/1eA |
| 0.100 J/cm² @Temperature -30.0 °C |
0.476 ft-lb/in² @Temperature -22.0 °F |
80*10*4mm, Cut; ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 58.0 µm/m-°C @Temperature -30.0 - 100 °C |
32.2 µin/in-°F @Temperature -22.0 - 212 °F |
ISO 11359-2 |
| CTE, linear, Transverse to Flow | 125 µm/m-°C @Temperature -30.0 - 100 °C |
69.4 µin/in-°F @Temperature -22.0 - 212 °F |
ISO 11359-2 |
| Deflection Temperature at 0.46 MPa (66 psi) | 131 °C | 268 °F | 80*10*4mm, Cut; ISO 75-1&2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 80.0 °C | 176 °F | 80*10*4mm, Cut; ISO 75-1&2 |
| Vicat Softening Point | 157 °C | 315 °F | 10N, 50°C/hr; ISO 306 |
Users viewing this material also viewed the following:
- Polymax® Maxelast® P3830 TPE, PP Overmold or Standalone use
- Styrolution Novodur® H701 ABS
- Teknor Apex APEX® 90-A472R-90-NT Polyvinyl Chloride, Flexible
- Teknor Apex Monprene® MP-2357-A Thermoplastic Elastomer
- A. Schulman INVISION™ VX-5075UI Soft Touch Polyolefin Thermoplastic
- Fainplast Compounds EVAtech 803S Ethylene Vinyl Acetate Foam
- Chosun Refractories C40 Special High-Density Gunning Castable
- BASF Elastollan® C-64D Polyester Type Polyurethane Elastomer
- 3M AC-236 Class B-4 Aerospace Sealant
Copyright © lookpolymers.com All Rights Reserved