SABIC Innovative Plastics REMEX VR4831 PBT

Category	Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT)
Manufacturer	SABIC Innovative Plastics (GE Plastics)
Trade Name
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	SABIC Innovative Plastics REMEX VR4831 PBT.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

15% Glass filled PBT, Flame retardant, UL Recognized, Utility grade, Black color only

Physical Properties	Metric	English	Comments
Specific Gravity	1.42 g/cc	1.42 g/cc	ASTM D792
Density	1.43 g/cc	0.0517 lb/inÂ³	ISO 1183
Filler Content	15 %	15 %	ASTM D229
Moisture Absorption	0.0400 %	0.0400 %	23Â°C / 50% RH; ISO 62
Water Absorption at Saturation	0.16 %	0.16 %	ISO 62
Linear Mold Shrinkage, Flow	0.0080 - 0.010 cm/cm @Thickness 3.20 mm	0.0080 - 0.010 in/in @Thickness 0.126 in	SABIC Method
Linear Mold Shrinkage, Transverse	0.0070 - 0.010 cm/cm @Thickness 3.20 mm	0.0070 - 0.010 in/in @Thickness 0.126 in	SABIC Method
Melt Flow	21.3 g/10 min @Load 5.00 kg, Temperature 265 Â°C	21.3 g/10 min @Load 11.0 lb, Temperature 509 Â°F	ASTM D1238
Melt Index of Compound	15 g/10 min @Load 5.00 kg, Temperature 265 Â°C	15 g/10 min @Load 11.0 lb, Temperature 509 Â°F	MVR [cm^3/10 min]; ISO 1133

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	61.0 MPa	8850 psi	Type I, 5 mm/min; ASTM D638
	63.0 MPa	9140 psi	5 mm/min; ISO 527
Tensile Strength, Yield	65.0 MPa	9430 psi	Type I, 5 mm/min; ASTM D638
	65.0 MPa	9430 psi	5 mm/min; ISO 527
Elongation at Break	3.0 %	3.0 %	Type I, 5 mm/min; ASTM D638
	3.4 %	3.4 %	5 mm/min; ISO 527
Elongation at Yield	2.5 %	2.5 %	5 mm/min; ISO 527
	2.6 %	2.6 %	Type I, 5 mm/min; ASTM D638
Tensile Modulus	4.32 GPa	627 ksi	5 mm/min; ASTM D638
	4.46 GPa	647 ksi	1 mm/min; ISO 527
Flexural Yield Strength	105 MPa	15200 psi	1.3 mm/min, 50 mm span; ASTM D790
	107 MPa	15500 psi	2 mm/min; ISO 178
Flexural Modulus	3.93 GPa	570 ksi	1.3 mm/min, 50 mm span; ASTM D790
	4.21 GPa	611 ksi	2 mm/min; ISO 178
Izod Impact, Notched	0.890 J/cm	1.67 ft-lb/in	ASTM D256
Izod Impact, Unnotched	5.35 J/cm	10.0 ft-lb/in	ASTM D4812
Izod Impact, Notched (ISO)	7.00 kJ/mÂ²	3.33 ft-lb/inÂ²	80104; ISO 180/1A
	4.00 kJ/mÂ² @Temperature -30.0 Â°C	1.90 ft-lb/inÂ² @Temperature -22.0 Â°F	80104; ISO 180/1A
Izod Impact, Unnotched (ISO)	34.0 kJ/mÂ²	16.2 ft-lb/inÂ²	80104; ISO 180/1U
	32.0 kJ/mÂ² @Temperature -30.0 Â°C	15.2 ft-lb/inÂ² @Temperature -22.0 Â°F	80104; ISO 180/1U
Charpy Impact, Notched	2.50 J/cmÂ²	11.9 ft-lb/inÂ²	Edgew 80104 sp=62mm; ISO 179/1eA
Dart Drop, Total Energy	12.0 J @Temperature 23.0 Â°C	8.85 ft-lb @Temperature 73.4 Â°F	ASTM D3763

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	43.0 Âµm/m-Â°C @Temperature -40.0 - 40.0 Â°C	23.9 Âµin/in-Â°F @Temperature -40.0 - 104 Â°F	ASTM E 831
	43.0 Âµm/m-Â°C @Temperature -40.0 - 40.0 Â°C	23.9 Âµin/in-Â°F @Temperature -40.0 - 104 Â°F	ISO 11359-2
CTE, linear, Transverse to Flow	128 Âµm/m-Â°C @Temperature -40.0 - 40.0 Â°C	71.1 Âµin/in-Â°F @Temperature -40.0 - 104 Â°F	ASTM E 831
	128 Âµm/m-Â°C @Temperature -40.0 - 40.0 Â°C	71.1 Âµin/in-Â°F @Temperature -40.0 - 104 Â°F	ISO 11359-2
Deflection Temperature at 0.46 MPa (66 psi)	150 Â°C	302 Â°F	Flatw 80104 sp=64mm; ISO 75/Bf
	150 Â°C @Thickness 3.20 mm	302 Â°F @Thickness 0.126 in	unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi)	120 Â°C	248 Â°F	Flatw 80104 sp=64mm; ISO 75/Af
	119 Â°C @Thickness 3.20 mm	246 Â°F @Thickness 0.126 in	unannealed; ASTM D648
Vicat Softening Point	143 Â°C	289 Â°F	Rate B/50; ASTM D1525
	143 Â°C	289 Â°F	Rate B/50; ISO 306
	144 Â°C	291 Â°F	Rate B/120; ISO 306
Flammability, UL94	V-0 @Thickness 1.50 mm	V-0 @Thickness 0.0591 in	UL 94 by SABIC-IP
	5VA @Thickness 2.30 mm	5VA @Thickness 0.0906 in	UL 94 by SABIC-IP