SABIC Innovative Plastics Prevex VFAX PPE+PS

Category Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polystyrene (PS)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name Prevex
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics Prevex VFAX PPE+PS.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
High impact strength. 180F (82C) HDT. Improved productivity/reliability.This data was supplied by SABIC-IP for the Americas region.
Physical Properties Metric English Comments
Specific Gravity 1.09 g/cc
1.09 g/cc
ASTM D 792
Linear Mold Shrinkage, Flow 0.0050 - 0.0070 cm/cm

@Thickness 3.20 mm
 0.0050 - 0.0070 in/in

@Thickness 0.126 in
 SABIC Method
Mechanical Properties Metric English Comments
Hardness, Rockwell R 115
115
ASTM D 785
Tensile Strength at Break 40.0 MPa
5800 psi
Type I, 50 mm/min; ASTM D 638
Tensile Strength, Yield 51.0 MPa
7400 psi
Type I, 50 mm/min; ASTM D 638
Elongation at Break 20 %
20 %
Type I, 50 mm/min; ASTM D 638
Elongation at Yield 5.8 %
5.8 %
Type I, 50 mm/min; ASTM D 638
Flexural Yield Strength 74.0 MPa
10700 psi
2.6 mm/min, 100 mm span; ASTM D 790
Flexural Modulus 2.34 GPa
339 ksi
2.6 mm/min, 100 mm span; ASTM D 790
Izod Impact, Notched 0.740 J/cm

@Temperature -30.0 °C
 1.39 ft-lb/in

@Temperature -22.0 °F
 ASTM D 256
2.88 J/cm

@Temperature 23.0 °C
 5.40 ft-lb/in

@Temperature 73.4 °F
 ASTM D 256
Izod Impact, Unnotched 12.7 J/cm

@Temperature 23.0 °C
 23.8 ft-lb/in

@Temperature 73.4 °F
 ASTM D 4812
Impact Test 1.00 J

@Temperature -30.0 °C
 0.738 ft-lb

@Temperature -22.0 °F
 Instrumented Impact Energy @ peak; ASTM D 3763
17.0 J

@Temperature 23.0 °C
 12.5 ft-lb

@Temperature 73.4 °F
 Instrumented Impact Energy @ peak; ASTM D 3763
Taber Abrasion, mg/1000 Cycles 134

@Load 1.00 kg
 134

@Load 2.20 lb
 CS-17; ASTM D 1044
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 91.0 °C

@Thickness 6.40 mm
 196 °F

@Thickness 0.252 in
 unannealed; ASTM D 648
Deflection Temperature at 1.8 MPa (264 psi) 82.0 °C

@Thickness 6.40 mm
 180 °F

@Thickness 0.252 in
 unannealed; ASTM D 648
Vicat Softening Point 105 °C
221 °F
Rate B/50; ASTM D 1525
UL RTI, Electrical 50.0 °C
122 °F
UL 746B
UL RTI, Mechanical with Impact 50.0 °C
122 °F
UL 746B
UL RTI, Mechanical without Impact 50.0 °C
122 °F
UL 746B
Flammability, UL94 V-2

@Thickness 1.47 mm
 V-2

@Thickness 0.0579 in
 UL 94
V-1

@Thickness 2.00 mm
 V-1

@Thickness 0.0787 in
 UL 94
Electrical Properties Metric English Comments
Arc Resistance 0.00 - 60 sec
0.00 - 60 sec
Tungsten, PLC code 7; ASTM D 495
Comparative Tracking Index 250 - 400 V
250 - 400 V
PLC code 2; UL 746A
Hot Wire Ignition, HWI 15 - 30 sec
15 - 30 sec
PLC code 3; UL 746A
High Amp Arc Ignition, HAI 60 - 120 arcs
60 - 120 arcs
surface, PLC code 1; UL 746A
High Voltage Arc-Tracking Rate, HVTR >= 150 mm/min
>= 5.91 in/min
PLC code 4; UL 746A